牌号简介 About |
---|
比竞争性的65/65级PVC/亚克力金属板具有更高的抗冲击性,加上具有无与伦比的耐刮擦性的整体颜色Boltaron 9815M是一种专用的阻燃挤压PVC/亚克力合金,用于飞机内部部件,满足FAA对易燃性、发烟性和热释放的严格要求。卓越的物理性能。它具有5.0 ft-lbs/in的抗冲击能力。(265 J/m)-高于竞争性65/65-符合要求的板材,额定值为3.0 ft-lbs/in。(159 J/m)-以及极高的成形性、一致的表面质量和无限的颜色范围。与FAR 25.853(d)额定值的纸张不同,FAR 25.853(d)额定值的纸张在层压至不同基材的透明盖膜上用金属油墨反向印刷,Boltaron 9815M由具有整体金属着色的盖膜组成,永久熔接至互补固体颜色的匹配“9815级”基材,防止分层,提供无与伦比的性能。耐刮擦性。由于9815M单片盖膜是Boltaron 9815纯色基板的“金属化”版本,因此金属颜色选择是无限的。Boltaron 9815M由世界领先的商用、军用和私人飞机和直升机制造商、运输公司和内部整修承包商指定,用于热成型、制造和机械加工的具有无与伦比的耐久性和金属外观的内部部件。 Greater impact resistance than competitive 65/65-rated PVC/Acrylic metallic sheets, plus integral color for unsurpassed scratch resistance Boltaron 9815M is a proprietary, fire retardant, extruded PVC/Acrylic alloy for aircraft interior components that meets stringent FAA requirements for flammability, smoke generation and heat release while exhibiting exceptional physical properties. It offers Izod Impact resistance of 5.0 ft lbs/in. (265 J/m)- higher than competitive 65/65- compliant sheets rated at 3.0 ft lbs/in. (159 J/m)- as well as extreme formability, consistent surface quality, and an unlimited range of colors. And unlike FAR 25.853 (d) rated sheet that is reverse-printed with metallic ink on clear cap film laminated to dissimilar substrate material, Boltaron 9815M is comprised of a cap film with integral metallic coloration, permanently fused to a matching "9815-grade" substrate of a complementary solid color, preventing de-lamination and offering unsurpassed scratch resistance. Since the 9815M monolithic cap film is a "metallized" version of Boltaron's 9815 solid color substrate, metallic color selection is unlimited. Boltaron 9815M is specified by the world's leading commercial, military and private aircraft and helicopter manufacturers, carriers and interior refurbishing contractors, for thermoformed, fabricated and machined interior components of unequalled durability and metallic appearance. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.57 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
270 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
76.7 | ℃ | ASTM D648 |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
3.0E-5 | 1/℃ | ASTM D696 |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
放热 exothermic |
FAR 25.853 | ||
2 min 2 min |
kW·min/m² | FAR 25.853 | |
Peak Peak |
kW/m² | FAR 25.853 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Ds Ds |
ASTM F814 | ||
1.5 min 1.5 min |
ASTM F814 | ||
4 min 4 min |
ASTM F814 | ||
成型温度 Forming temperature |
℃ | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
华友钴业募资建锂电材料项目
2022-02-26 2月21日,华友钴业发布公告,公司公开发行可转换公司债券已获得中国证券监督管理委员会核准,拟募集资金总额为76亿元,扣除发行费用后将用于年产5万吨高镍型动力电池三元正极材 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |