牌号简介 About |
---|
NYCOA 5113 HS是一种13%玻璃纤维增强、热稳定、冲击改性尼龙66树脂,用于注塑成型。NYCOA 5113 HS是专门为改善玻璃填充尼龙66的延展性和冲击强度而设计的。典型应用包括鞋底、五金件和汽车引擎盖应用。 NYCOA 5113 HS is a 13% glass fiber reinforced, heat stabilized, impact modified Nylon 66 resin used for injection molding. NYCOA 5113 HS has been specifically formulated for improved ductility and impact strength vs standard grades of glass filled Nylon 66. Typical applications include shoe sole plates, hardware items and automotive under the hood applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.22 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
ASTM D955 | ||
MD MD |
0.70 | % | ASTM D955 |
TD TD |
1.2 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
1.3 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
6.4mm 6.4mm |
160 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
熔融温度 Melting temperature |
℃ | DSC | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 3 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2,0 in/min |
【新闻资讯】查看全部
赢创投资于现代化的Rohacell泡沫生产设施
2022-03-28 赢创(德国埃森)正在为其在德国达姆施塔特生产的用于纤维增强复合材料的高性能Rohacell泡沫投资建设一个新的现代化生产设施。同时,1972年投入使用的原生产厂的部分设备将被关闭 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |