| 牌号简介 About |
|---|
| Purell PE 3020 K是一种非加成的低密度聚乙烯，具有高刚性、良好的光学性能和良好的耐化学性。以颗粒形式交付。毫无例外，制药、医疗器械、实验室和诊断领域的所有潜在应用活动都必须首先与相关技术和业务联系人进行讨论。要讨论医疗/药物应用，请联系：当地经销商或当地LyondellBasell联系人。 Purell PE 3020 K is a non-additivated, low density polyethylene with high rigidity, good opticals and good chemical resistance. It is delivered in pellet form. Without exception, all potential activities for applications in the pharmaceutical, medical device, laboratory and diagnostics area have to be discussed with the relevant Technical and Business contacts first. To discuss a medical/pharmaceutical application please contact: your local Distributor or your local LyondellBasell contact. |
产品描述 Product Description
用途：医疗/护理用品;薄膜;药物;
性能特点： 机械强度好; 耐化学性; 光学性能; 热封性好; 易加工; Good Rigidity,Excellent Processability,Good heat sealing,Optical performance,Solvent resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.928 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
4.0 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
300 | MPa | ISO 527-2 |
|
摩擦系数 friction coefficient |
|||
|
吹塑薄膜 Blown film |
> 0.80 | ISO 8295 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
15 to 40 µm | ||
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
屈服 yield |
MPa | ISO 527-2 | |
|
MD，50 µm，吹塑薄膜 MD, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，50 µm，吹塑薄膜 TD, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
|
落锤冲击 Drop hammer impact |
|||
|
50 µm，吹塑薄膜 50 µ m, blow molded film |
g | ASTM D1709 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 3146 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
ASTM D2457 | ||
|
20°，50 µm，吹塑薄膜 20 °, 50 µ m, blow molded film |
ASTM D2457 | ||
|
60°，50.0 µm，吹塑薄膜 60 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
50 µm，吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
破坏能量 Destruction energy 2 |
|||
|
50.0 µm 50.0 µm 2 |
J/cm | DIN 53373 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Blown Film |
|
【新闻资讯】查看全部 
聚乙烯氧化生物降解技术助力农用薄膜回收
2017-06-20 中国广州华南农业大学研究人员研究了一种有效、环保和可降解的聚烯烃材料帮助解决农用聚烯烃难于回收问题。 聚烯烃广泛用于农业应用(例如，用于温室，覆盖或隧道膜)。事实上，据报道，80%的塑料覆盖物由聚烯烃(例如聚乙烯)制成。虽然这种材料可以促进良好的收获，但大多数聚烯烃塑料地膜的处理是有问题的。 研究人员使用PMMA表面改性TiO2纳米粒子作为添加剂，以促进聚乙烯的降解。他们发现，由LDPE制成的复合膜和这些改性纳米粒子在紫外线照射后比纯LDPE样品显示出更大的 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |