牌号简介 About |
---|
说明:MARPOL® HDF 504是一种双模高密度聚乙烯(HMW-HDPE)树脂,设计用于高镖冲击强度和良好的加工特性。MARPOL® HDF 504在整体物理性能方面具有良好的平衡性,为薄膜应用提供了良好的刚度。推荐用途:T恤袋、垃圾桶衬垫、工业衬垫和重型袋子。 Description: MARPOL® HDF 504 is a bi-modal HMW-HDPE resin designed for high dart impact strength and good processing characteristics. MARPOL® HDF 504 is well balanced in overall physical properties and provides good stiffness for thin gauge film applications. Recommended Applications: T-shirt bags, trash can liners, industrial liners, and heavy bags. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.949 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.040 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
8.5 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂 MD, fracture |
62.1 | MPa | ASTM D882 |
TD,断裂 TD, fracture |
28.3 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD MD |
g | ASTM D1922 | |
TD TD |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | DSC |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
独山子石化高科技产品添彩百姓重生活
2018-03-02 在南方上大学的女儿刚开学,吴女士就跟老公念叨:“也不知道女儿最喜欢的新疆酸奶,那边能不能买到?” “能,女儿说,不仅有,还原汁原味呢。”在独山子石化公司研究院工作的老公张先生说。 吴女士半信半疑地问:“这酸奶运到几千公里外能有在家门口喝到的新鲜吗?”张先生说:“奥秘全在这酸奶包装上。” 过去,酸奶常用玻璃瓶装,遇热易炸,遇冷易裂,还不好保鲜。现在,由碳酸钙和聚烯烃混合而成的新型软包装材料――爱克林,很好地解决了这些问题。这种新型软包装材料中至 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |