solef ® 460/461 PVDF均聚物具有较高的熔体粘度,通常采用挤塑加工。 Solef® 460/461 PVDF homopolymer has high melt viscosity and is typically processed by extrusion. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
75 | ASTM D2240 | |
拉伸模量 Tensile modulus 2 |
|||
23℃ 23℃ 2 |
1310 | MPa | ASTM D638 |
拉伸强度 tensile strength 2 |
|||
断裂,23℃ Fracture, 23 ℃ 2 |
41.0 | MPa | ASTM D638 |
屈服,23℃ Yield, 23 ℃ 2 |
48.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂,23℃ Fracture, 23 ℃ 2 |
100 | % | ASTM D638 |
屈服,23℃ Yield, 23 ℃ 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 2 |
|||
23℃ 23℃ 2 |
MPa | ASTM D790 | |
弯曲强度 bending strength 2 |
|||
屈服,23℃ Yield, 23 ℃ 2 |
MPa | ASTM D790 | |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态 With oneself - dynamic |
ASTM D1894 | ||
与自身 - 静态 With oneself - static |
ASTM D1894 | ||
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D4065 | |
熔融温度 Melting temperature |
℃ | ASTM D3418 | |
结晶峰温度 Crystallization peak temperature 12 |
|||
DSC DSC 12 |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
比热 specific heat |
J/kg/℃ | ASTM D3418 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM D433 | |
结晶热 Crystallization heat |
J/g | ASTM D3418 | |
融合热量 Fusion heat |
J/g | ASTM D3418 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity 3 |
|||
23℃ 23℃ 3 |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
23 ℃,3.2 mm 23 ℃,3.2 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
23 ℃,1 MHz 23 ℃,1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,21.6kg 230℃,21.6kg |
g/10min | ASTM D1238 | |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
% | ASTM D570 | |
熔体表观粘度 Apparent viscosity of melt |
|||
232℃,100 sec^-1 232℃,100 sec^-1 |
Pa·s | ASTM D3835 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 50% RH |
【新闻资讯】查看全部
2020年快递可降解绿色包装资料使用将达50%
2017-11-06 从邮政局网站获悉,国家邮政局、国家发展改革委、科技部、工业和信息化部、环境保护部、住房与城乡建设部、商务部、国家质量监督检验检疫总局、国家认证认可监督管理委员会、国家标准化管理委员会日前联合发布《关于协同推进快递业绿色包装工作的指导意见》。意见提出每年11月第一周定为“绿色快递宣传周”,2020年可降解绿色包装材料应用比例将达50%。 《指导意见》明确了“十三五”期间快递业绿色包装工作要实现的三大目标,即:绿色化、减量化、可循环取得明显效果,科技创新和应用水平大幅提升,治理 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |