牌号简介 About |
---|
Formolene® L62009E2是采用气相技术制备的通用薄膜级线性低密度。该树脂在拉伸到薄规格时表现出优异的韧性和强度。Formolene® L62009E2符合美国食品和药物管理局在21CFR 177.1520中规定的所有要求,包括用于直接食品接触的聚烯烃制品的安全使用。 Formolene® L62009E2 is a general-purpose film grade linear low density made using gas-phase technology. The resin exhibits excellent toughness and strength when drawn down to thin gauges. Formolene® L62009E2 meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.919 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.95 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂 MD, fracture |
32.8 | MPa | |
TD,断裂 TD, fracture |
24.0 | MPa | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ||
TD,断裂 TD, fracture |
% | ||
落锤冲击 Drop hammer impact |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD MD |
g | ||
TD TD |
g | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D523 | ||
雾度 Haze |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blow(up Ratio) Blow(up Ratio) |
备注 |
---|
1 additives talc based |
2 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
巴斯夫中间体产品碳足迹远低于全球市场平均值
2022-06-09 包括具体产品从摇篮到大门的碳排放分析 市场比较显示中间体系列产品占据优势 巴斯夫已计算出大部分中间体产品中单个产品的碳足迹(PCF)[1],并将结果与相应第三方产品的市场平 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |