SABIC PP化合物G3240A SABIC® PPcompound G3240A是一种40%的短玻璃纤维增强聚丙烯,用于发动机罩和结构应用。母材为聚丙烯均聚物,可用标准黑色。玻璃纤维以化学方式耦合到PP基体SABIC® PPcompound G3240A是指定的汽车级。SABIC PP化合物G3240A SABIC PP化合物G3240A是一种通用的、40%玻璃填充、化学耦合、热稳定的均聚聚丙烯化合物。IMDS ID是139448304。 SABIC® PPcompound G3240A is a 40% short glass fiber reinforced Polypropylene for unter-the-hood and structural applications. The base material is a PP homopolymer and is available in standard black. The glass fibres are chemically coupled to the PP matrix SABIC® PPcompound G3240A is a designated automotive grade. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.22 | g/cm³ | ASTM D792 |
密度 Density |
1.22 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
11 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
Internal Method | ||
TD:23℃,48 hrs TD:23℃,48 hrs |
0.80 | % | 内部方法 |
MD:23℃,48 hrs MD:23℃,48 hrs |
0.40 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture |
MPa | ISO 527-2/1A/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 4 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ 6 |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ 7 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 6 |
ISO 180/1A | ||
23℃,3.2mm 23℃,3.2mm 8 |
J/m | ASTM D256 | |
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
|||
23℃,3.2 mm 23℃,3.2 mm 8 |
J/m | ASTM D4812 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 9 |
|||
23℃,Energy at Peak Load 23℃,Energy at Peak Load 9 |
J | ASTM D3763 | |
落锤冲击 Drop hammer impact 10 |
|||
23℃ 23℃ 10 |
J | ASTM D5420 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 6 |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed 6 |
℃ | ISO 75-2/A | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed 6 |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-30~100℃ TD:-30~100℃ |
1/℃ | ISO 11359-2 | |
MD:-30~100℃ MD:-30~100℃ |
1/℃ | ISO 11359-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2,0 in/min |
3 类型 1, 2,0 in/min |
4 0,079 in/min |
5 0,051 in/min |
6 方法 I (三点负荷) |
7 80*10*4mm, Cut |
8 80*10*4 mm, Cut |
9 63.5*12.7*3.2mm, Cut |
10 7,22 ft/sec |
11 0.625"d tup |
【新闻资讯】查看全部
中芯国际全线芯片代工全线涨价 去年中芯国际净利润同比增长141.5%
2021-04-07 搜料网资讯: 台积电要将12英寸晶圆每片上涨400美元,而且每个季度都有调整的可能。中芯国际已经告知客户,从4月1日起将全面涨价;究其原因与2020年下半年受到美国实体名单管制导致 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |