牌号简介 About |
---|
湿粒级。由于这些等级的材料比干颗粒材料的“含气性”小,因此它们特别适用于厚型塑件,如马桶座。它们也被推荐用于塑封,因为它们的细粉自由流动粉末特性允许精确计量非常小的装料重量。 Wet granulated grade. As these grades are less "gassy" than dry granulated materials they are particularly suitable for thick section mouldings such as toilet seats. They are also recommended for moulding closures because their fines free flowing powder properties allow accurate metering of very small charge weights. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.52 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.70 | g/cm³ | ISO 60 |
紧缩率 Shrinkage rate |
2.2 | ISO 171 | |
收缩率 Shrinkage rate |
ISO 2577 | ||
-- -- 2 |
0.76 | % | ISO 2577 |
-- -- 3 |
0.73 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
Cold Cold 4 |
mg | ISO 62 | |
Cold Cold 5 |
mg | DIN 53472 | |
Hot Hot 6 |
mg | ISO 62 | |
后收缩 Post contraction |
ISO 2577 | ||
-- -- 2 |
% | ISO 2577 | |
-- -- 7 |
% | ISO 2577 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180/C | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Ae | |
Martens Temperature Martens Temperature |
℃ | DIN 43458 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | DIN 53483 | |
体积电阻率 Volume resistivity |
ohms·cm | DIN 53483 | |
介电强度 Dielectric strength |
IEC 60243-1 | ||
-- -- 2 |
kV/mm | IEC 60243-1 | |
-- -- 8 |
kV/mm | IEC 60243-1 | |
耗散因数 Dissipation factor |
DIN 53483 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60167 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
3.00 mm 3.00 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index 9 |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Preheated powder |
3 Cold powder |
4 96 hr @ 23°C |
5 24 hr @ 23°C |
6 30 min @ 100°C |
7 (48 hr) Preheated powder |
8 (90°C) Preheated powder |
9 程序 A |
【新闻资讯】查看全部
“深海一号” 探寻超深海能源宝藏
2021-07-06 搜料网资讯: 最大排水量约为3艘中型航母,拥有3项世界首创,集海洋石油工程之大成,从300米向1500米超深水跨越大国重器深海一号来了! 近日,我国自营勘探开发的首个1500米超深水 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |