牌号简介 About |
---|
F5001是采用滚圆工艺生产的通用挤出薄膜级高密度聚乙烯。该牌号具有良好的加工性能和机械强度。F5001可作为高密度聚乙烯薄膜的共混树脂,用于包装应用。 F5001 is a general purpose extrusion film grade HDPE produced by the Spherilene Technology. This grade is characterized by good processability and mechanical strength. F5001 can be used as blending resin in HDPE film for packaging application. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.950 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.1 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
450 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融峰值温度 Melting peak temperature |
131 | ℃ | ASTM D3418 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
61 | ASTM D2240 | |
拉伸强度 tensile strength 1 |
ASTM D638 | ||
屈服,模压成型 Yield, molding |
MPa | ||
断裂,模压成型 Fracture, molded |
MPa | ||
拉伸应变 Tensile strain 2 |
|||
断裂,模压成型 Fracture, molded 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 4 |
【新闻资讯】查看全部
扬子石化车间锅炉中控室声光报警响起
2019-02-20 “嘟嘟嘟嘟”1月24日上午10点50分,扬子石化烯烃厂公用工程车间锅炉中控室突然声光报警响成一片,B台辅锅火炬气事故电磁阀突然关闭,导致火炬气压力高报警,B炉联锁停炉,锅炉班长赵�F立即向厂调度及车间领导杨希铭汇报。 烯烃厂调度台得知信息后立即通知相关单位,启动厂级应急预案,同时联系生产调度处最大量引入3A线蒸汽,努力保持下游乙烯联合装置稳定运行。而此时,在乙烯联合装置控制室,压缩岗位班长李欣乐检查发现,超高压蒸汽压力从11兆帕急剧下降至10.5兆帕,立即向值班长汇报,值班 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |