牌号简介 About |
---|
可制版,成型级PC/ABS Material Type: Black color base (alkali) resistance grade fluoroelastomer compound, hardness Shore A 65~75. Based on peroxide curable fluoroelastomer with high fluorine content. Features: Short post cure time Excellent mold flow and mold release, resulting in less flash Extraordinary chemical resistance: Alkali Alcohol Fuel Steam Acids Chemicals containing amines, aromatic. Process Methods: Suitable for compression, transfer, injection and extrusion molding process. Applications: Heat exchanger gasket and other parts require chemical, steam and acid resistance. Lab Testing Curing Condition: Press Curing: 10min@170°C. Oven: (1+4)hrs@230°C |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.98 | g/cm³ | ASTM D792 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
70 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
14.0 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
230 | % | ASTM D412 |
压缩形变 Compression deformation 2 |
|||
200℃,70 hr 200℃,70 hr 2 |
32 | % | ASTM D395 |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
250℃,70 hr 250℃,70 hr |
% | ASTM D573 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
250℃,70 hr 250℃,70 hr |
% | ASTM D573 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
|||
250℃,70 hr 250℃,70 hr |
ASTM D573 | ||
拉伸强度的变化率 The rate of change in tensile strength |
|||
23℃,70 hr,C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 | |
极限伸长率的变化率 Change rate of ultimate elongation |
|||
23℃,70 hr,C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 | |
邵氏硬度的变化率 The rate of change in Shore hardness |
|||
23℃,70 hr,在基准燃料C中 23 ℃, 70 hr, in reference fuel C |
ASTM D471 | ||
体积变化 Volume change |
|||
23℃,70 hr,C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
我国甲甲酯(MMA)行业近年来蓬勃展开
2018-11-28 甲基丙烯酸甲酯(MMA)是一种重要的化工原料。主要用于生产有机玻璃(PMMA)、聚氯乙烯助剂ACR、甲基丙烯酸甲酯一苯乙烯一丁二烯共聚物(MBS)等。受国内导光板、光导纤维、液晶显示屏、水性涂料等下游市场的增长的带动,我国甲甲酯(MMA)行业近年来蓬勃发展。 目前我国MMA的生产技术是丙酮氰醇法(ACH法),异丁烯法(C4法)共存。同时乙烯法和醋酸甲酯法也都通过了中试阶段。 丙酮氰醇法工艺技术比较成熟、稳定简单,约占我国的60%。但是缺点同样明显:原料氢氰酸 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |