公司信息及水印
牌号简介 About |
---|
Valox 4031树脂Valox 4031是一种30%高强度玻璃纤维增强PBT注塑树脂,具有优异的强度、刚度和耐热性。应用:电器手柄,聚光灯,电机。 VALOX 4031 is a 30% high strength glass fibre reinforced PBT injection moulding resin with excellent strength, stiffness and heat resistance. Applications: appliance handles, spotlights, electric motors. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ 10 |
6.0 | kJ/m² | ISO 179/1eA |
-30℃ -30℃ |
12 | kJ/m² | ISO 179/2C |
23℃ 23℃ 10 |
7.0 | kJ/m² | ISO 179/1eA |
23℃ 23℃ |
12 | kJ/m² | ISO 179/2C |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ 10 |
55 | kJ/m² | ISO 179/1eU |
-30℃ -30℃ |
kJ/m² | ISO 179/2U | |
23℃ 23℃ 10 |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/2U | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
0℃ 0℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 11 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
0℃ 0℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D4812 | ||
-30℃ -30℃ |
J/m | ASTM D4812 | |
23℃ 23℃ |
J/m | ASTM D4812 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 11 |
ISO 180/1U | ||
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,100 mm跨距 0.45 MPa, unannealed, 100 mm span 12 |
℃ | ISO 75-2/Be | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 13 |
℃ | ISO 75-2/Bf | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
ISO 11359-2 | ||
-40 到 40℃ -40 to 40 ℃ |
cm/cm/℃ | ISO 11359-2 | |
23 到 80℃ 23 to 80 ℃ |
cm/cm/℃ | ISO 11359-2 | |
23 到 150℃ 23 to 150 ℃ |
cm/cm/℃ | ISO 11359-2 | |
MD MD |
ISO 11359-2 | ||
-40 到 40℃ -40 to 40 ℃ |
cm/cm/℃ | ISO 11359-2 | |
23 到 80℃ 23 to 80 ℃ |
cm/cm/℃ | ISO 11359-2 | |
23 到 150℃ 23 to 150 ℃ |
cm/cm/℃ | ISO 11359-2 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
ASTM D149 | ||
0.8 mm,在油中 0.8 mm in oil |
kV/mm | ASTM D149 | |
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ASTM D149 | |
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
介电强度 Dielectric strength |
IEC 60243-1 | ||
0.8 mm,在油中 0.8 mm in oil |
kV/mm | IEC 60243-1 | |
1.6 mm,在油中 1.6 mm in oil |
kV/mm | IEC 60243-1 | |
3.2 mm,在油中 3.2 mm in oil |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
60 Hz 60 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
60 Hz 60 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc resistance 16 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
6.00 mm 6.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
填充物 Filler |
% | ASTM D229 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 3 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 4 |
|||
断裂 fracture 4 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
屈服 yield |
MPa | ISO 527-2/5 | |
屈服 yield 4 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
屈服 yield 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 6 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
弯曲强度 bending strength 6 |
ISO 178 | ||
断裂,50 mm跨度 Fracture, 50 mm span 5 |
MPa | ASTM D790 | |
屈服,50 mm跨度 Yield, 50 mm span 5 |
MPa | ASTM D790 | |
-- -- 7 |
MPa | ISO 178 | |
-- -- 8 |
MPa | ISO 178 | |
断裂弯曲应变 Fracture bending strain 9 |
% | ISO 178 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ISO 2039-2 | ||
球压硬度 Ball hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039-1 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
密度 Density |
g/cm³ | ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
266℃,5.0kg 266℃,5.0kg |
g/10min | ASTM D1238 | |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
250℃,2.16 kg 250℃,2.16 kg |
cm³/10min | ISO 1133 | |
250℃,5 kg 250℃,5 kg |
cm³/10min | ISO 1133 | |
265℃,5 kg 265℃,5 kg |
cm³/10min | ISO 1133 | |
收缩率 Shrinkage rate 2 |
|||
TD TD 2 |
% | 内部方法 | |
MD MD 2 |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
熔体表观粘度 Apparent viscosity of melt |
|||
260℃,1500 sec^-1 260℃,1500 sec^-1 |
Pa·s | ISO 11443 | |
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.8 MPa,未退火,100 mm跨距 1.8 MPa, unannealed, 100 mm span 12 |
℃ | ISO 75-2/Ae | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 13 |
℃ | ISO 75-2/Af | |
-- -- |
℃ | ASTM D1525 14 | |
-- -- |
℃ | ASTM D1525 15 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Tensile Bar |
3 0.20 in/min |
4 类型 1, 0.20 in/min |
5 0.051 in/min |
6 0.079 in/min |
7 Yield |
8 Break |
9 2 mm/min |
10 80*10*4 sp=62mm |
11 80*10*4 |
12 120*10*4 mm |
13 80*10*4 mm |
14 标准 B (120°C/h), 载荷2 (50N) |
15 速率 A (50°C/h), 载荷2 (50N) |
16 钨电极 |
【新闻资讯】查看全部
英国拟加大禁塑步伐 对一次性使用的塑料产品征税
2018-03-22 英国财政大臣哈蒙德最近放出风声,表示要考虑对一次性使用的塑料产品征税。 据称,一生专注于自然与科学探索节目制作而封爵的老爷子大卫・艾登堡说服了女王,要首先在自己的私人地盘上禁止使用一次性的塑料吸管。艾登堡之所以有此想法,缘于对海洋生物惨遭塑料垃圾困扰的震惊。 禁塑成为热点,反映出发达经济体的绿色革命正与互联网信息技术革命几乎同步进行。能源和环保材料的使用,虽然热度逊于互联网,却更真切地关乎这个世界的未来。不少发达国家新能源占能源消费的比例已经相当高,一些发达 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |