牌号简介 About |
---|
符合ISO 1043-1的化学缩写:POM成型化合物ISO 9988-POM-K,M-GNS,02-002 POM共聚物注射成型型,用聚四氟乙烯改性;对溶剂、燃料和强碱具有良好的耐化学性,以及良好的抗水解性;对热降解和氧化降解具有较高的抵抗力;对于滑动组合具有非常低的w摩擦系数。自然和厚度超过1.57 mm的UL注册为UL 94 HB,温度指数为UL 746 B,电气105°C,机械95°C(拉伸冲击)和100°C(拉伸)。厚度大于1 mm时,燃烧速率为ISO 3795和FMVSS 302<100 mm/min。适用范围:适用于摩擦系数非常低的滑动组合。fmvss=联邦机动车安全标准(美国)ul=保险商实验室(美国) Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988- POM-K, M-GNS, 02-002 POM copolymer Injection molding type, modified with PTFE; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation; for sliding combinations with very low coefficient of friction. UL-registration in natural and a thickness more than 1.57 mm as UL 94 HB, temperature index UL 746 B electrical 105 °C, mechanical 95 °C (tensile impact) and 100 °C (tensile). Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm. Ranges of applications: For sliding combinations with very low coefficient of friction. FMVSS = Federal Motor Vehicle Safety Standard (USA) UL = Underwriters Laboratories (USA) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.51 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
6.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
1.7 | % | ISO 294-4 |
MD MD |
2.0 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
0.65 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/1A/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/1A/50 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
% | ISO 527-2/1A/50 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
【新闻资讯】查看全部
每天2000万份!外卖塑料袋可掩盖168个足球场
2017-09-22 每天超过2000万份外卖,用掉的餐盒摞起来足以从地球到国际空间站转3个半来回,塑料袋可覆盖168个足球场……我们每天吃外卖产生的垃圾竟是如此巨量,令人惊叹! “新华视点”记者调查发现,包含了剩菜剩饭、沾了油污的外卖餐盒连同塑料袋,无论质量好坏,都难以回收,只能和其他生活垃圾混杂在一起处理,严重加剧了环境负担。 外卖每天用的塑料袋可覆盖168个足球场 一个工作日中午,记者在北京金融街一家金融公司总部楼下采访发现 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |