| 牌号简介 About |
|---|
| TC-9462 A/B是一种双组分聚氨酯铸造化合物，专门为高耐磨性和抗冲击性而配制。建议用于高耐磨零件和衬里的铸造。本产品是一种安全、易于操作、室温混合和固化系统，不含TDI、MDI、MDA或MOCA。TC-9462 A/B对典型的环境湿度相对不敏感，可制成良好的无空隙零件。由于本产品具有优异的韧性和耐磨性，用TC-9462 A/B铸造的铸件特别适用于采矿和矿物加工行业。特点：抗冲击性强，粘度低，特别坚韧，耐磨性好，不含TDI、MDI、MDA或MOCA，易于处理室温混合和无汞固化。 TC-9462 A/B is a two-component urethane casting compound that is specifically formulated for high abrasion and impact resistance.It is recommended for use in the casting of highly wear-resistant parts and linings. This product is a safe, easy-to-handle, room temperature mixing and curing system that does not contain TDI, MDI, MDA, or MOCA. TC-9462 A/B is relatively insensitive to typical environmental moisture and will make good void-free parts. Because of this product's exceptional toughness and abrasion resistance, castings made with TC-9462 A/B are particularly suitable for mining and mineral process industries. High impact resistance Low viscosity Exceptionally tough, abrasion resistant Easy to handle Room temperature mixing and curing Mercury free |
产品描述 Product Description
用途：矿业应用;耐磨衬板;
颜色：清晰/透明,琥珀色
性能特点： 耐磨; 超高韧性; 低粘度; 冲击性能好; High impact resistance,Low Viscosity,Ultra high toughness,Good wear resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
|||
|
-- -- 2 |
1.05 | g/cm³ | ASTM D792 |
|
-- -- 3 |
1.09 | g/cm³ | ASTM D792 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.20 | % | ASTM D2566 |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
撕裂强度 tear strength |
102 | kN/m | ASTM D624 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
750 | J/m | ASTM D256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热固组件 Thermosetting components |
|||
|
部件 A Component A |
|||
|
部件 B Component B |
|||
|
贮藏期限 Storage period |
wk | ||
|
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
25℃ 25℃ |
cP | ||
|
25℃ 25℃ 2 |
cP | ||
|
25℃ 25℃ 3 |
cP | ||
|
脱模时间 stripping time |
|||
|
25℃ 25℃ |
min | ||
|
后固化时间 Post curing time |
|||
|
71℃ 71℃ |
hr | ||
|
胶凝时间 Gelation time |
min | 内部方法 | |
|
工作时间 working hours 4 |
|||
|
25℃ 25℃ 4 |
min | 内部方法 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ASTM D2240 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Part A |
| 3 Part B |
| 4 100 g mass |
|
【新闻资讯】查看全部
北京工商局流通范畴塑料制品类商品质量抽检后果公示
2015-11-25 在2015年流通领域商品质量抽检工作中，我局对北京市场上销售的塑料制品类商品进行了抽检。抽检结果显示，标称商标为巧妙、乐润、清禾、南星等的塑料商品存在不符合相关标准的问题，主要涉及塑料袋的有效长度偏差、有效宽度偏差、抗渗漏性能、跌落性能等项目不符合相关标准要求。 我局将依据《产品质量法》的相关规定，对不合格商品的销售者进行处罚，同时督促全市销售者做好相同生产者相同型号不合格商品的退市工作。对于拒不履行退市义务的销售者，我局将依法予以查处。公示的不合格商品生产企业和有关经销单 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付