牌号简介 About |
---|
GB311U是一种30%化学耦合玻璃纤维增强聚丙烯化合物,用于注塑成型。这种材料在高温下也表现出优良的机械性能。 Fibremod GB311U is a 30% chemically coupled glass fibre reinforced polypropylene compound intended for injection moulding. This material shows excellent mechanical properties also at elevated temperatures. The product is available in standard black 8229. Applications Fibremod GB311U has been developed especially for demanding applications in the automotive industry. Technical components exposed to high heat and loads Structural parts Washing machine parts Special Features High heat stabilised Detergent resistant |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.12 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
2.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate 2 |
Internal Method | ||
TD:2.0 mm TD:2.0 mm |
1.0 | % | 内部方法 |
MD:2.0 mm MD:2.0 mm |
0.20 | % | 内部方法 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃,注塑成型 -30 ℃, injection molding |
8.0 | kJ/m² | ISO 179/1eA |
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 179/1eA | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 179/1eU | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 180-1A | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ISO 306/A | |
-- -- |
℃ | ISO 306/B | |
Melt Energy Melt Energy |
kJ/kg | ISO 11357 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾化 atomization |
|||
16 hrs,100℃ 16 hrs,100℃ |
mg | DIN 75201 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
排放 discharge |
µg/g | VDA 277 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 3 |
|||
注塑成型 injection molding 3 |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 3 |
|||
屈服,注塑成型 Yield, injection molding 3 |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain 3 |
|||
断裂,注塑成型 Fracture, injection molding 3 |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 4 , 3 |
|||
注塑成型 injection molding 4 , 3 |
MPa | ISO 178 | |
弯曲强度 bending strength 3 |
|||
注塑成型 injection molding |
MPa | ISO 178 | |
球压硬度 Ball hardness |
|||
H 132/10 H 132/10 |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 150x80x2 mm |
3 Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
4 0.079 in/min |
【新闻资讯】查看全部
1~11月中国出口塑料制品2377亿元 同比增13.3%
2017-12-12 据中国海关总署最新数据显示,2017年1~11月,中国货物贸易进出口总值25.14万亿元人民币(下同),比去年同期增长15.6%。 其中,出口13.85万亿元,增长11.6%;进口11.29万亿元,增长20.9%;贸易顺差2.56万亿元,收窄16.7%。 11月当月,中国进出口总值2.6万亿元,增长12.6%。其中,出口1.43万亿元,增长10.3%;进口1.17万亿元,增长15.6%;贸易顺差2636亿元,收窄8.4%。 < |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |