FRIANYL® A3 V0是一种未填充的聚酰胺66(尼龙66)化合物,阻燃,无卤素和红磷,UL列出的v0。该化合物用于注塑成型。FRIANYL® A3 V0主要为电气和电子工业设计。它也适用于汽车或工业和消费者应用。 FRIANYL® A3 V0 is an unfilled Polyamide 66 (Nylon 66) compound, flame retardant, halogen and red phosphorous free, UL listed V0. This compound is intended for injection molding. FRIANYL® A3 V0 is primarily designed for the Electrical and Electronic industry. It is also suitable for Automotive or Industrial & Consumer applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.17 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:23℃ TD:23℃ |
1.7 | % | ISO 294-4 |
MD:23℃ MD:23℃ |
1.5 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
6.0 | % | ISO 62 |
23℃,24hr 23℃,24hr |
2.0 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
连续使用温度 Continuous use temperature 2 |
℃ | IEC 60216 | |
球压测试 Ball pressure test |
IEC 60695-10-2 | ||
125℃ 125℃ |
IEC 60695-10-2 | ||
165℃ 165℃ |
IEC 60695-10-2 | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity 3 |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
2 mm 2 mm |
kV/mm | IEC 60243-1 | |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
3.20 mm,解决方案 A 3.20 mm, solution A |
V | IEC 60112 | |
针焰测试 Needle flame test |
IEC 60695-11-5 | ||
1.00 mm 1.00 mm |
IEC 60695-11-5 | ||
2.00 mm 2.00 mm |
IEC 60695-11-5 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.40 mm 0.40 mm |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.80 mm 0.80 mm |
℃ | IEC 60695-2-12 | |
3.2 mm 3.2 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 20000 hr |
3 23°C |
【新闻资讯】查看全部
陶氏化学收购杜邦未来将逐步转型特种化工领域
2016-12-08 “陶氏已经向特种化工企业进一步转型。”12月6日,陶氏大中华区总裁林育麟告诉21世纪经济报道记者。 今年以来陶氏对道康宁和杜邦两个跨国企业的收购,让其转型进一步加速。据记者了解,道康宁已经完成重组,而价值600亿美元的杜邦合并案还在欧盟等机构的审查中。 林育麟介绍,人才是陶氏业务的核心要素,决定着能否抓住机遇,为中国市场和客户提供价值。他是在当天陶氏化学(中国)获得2017年度中国“杰出雇主”认证后作出上述表示的。 “将国际油价波动的风险降低 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |