| 牌号简介 About |
|---|
| SABIC® PP 505P是一个多用途的挤出和注塑应用等级。SABIC® PP 505P具有优异的拉伸性能，适用于胶带、捆扎带、高强度纱线的挤压，也适用于热成型制品。对于注塑成型零件SABIC® PP 505P，其硬度适中，抗冲击性好，表面硬度非常好。SABIC PP505P适用于瓶盖、瓶盖和家用器皿的生产。SABIC® PP 505P是一种低MFI等级，通常用于板材和热成型等挤压应用。SABIC® PP 505P通常用于奶制品、花盆、黄色脂肪和一次性盘子和杯子。然而，客户也将此等级与滑石和碳酸钙等填料结合使用。 SABIC® PP 505P is a multi purpose grade for extrusion and injection moulding applications. SABIC® PP 505P provides an excellent stretch ability and is suitable for extrusion of tapes, strapping, high tenacity yarns but also for thermoformed articles. For injection moulded parts SABIC® PP 505P shows a moderate stiffness, good impact resistance and very good surface hardness. SABIC PP505P is suitable for production of caps and closures and house ware articles. SABIC® PP 505P is a low mfi grade typically used in extrusion applications like sheet and thermoforming. SABIC® PP 505P is typically used in dairy, flower pots, yellow fats and disposables plates and cups. However, customers use this grade also in combination with fillers like Talc and CaCO3. |
产品描述 Product Description
用途：杯子;家用货品;一次性酒具;片材;带子;线;护罩;皮带材料;外壳;
加工条件：挤出 Extrusion
性能特点： 宽分子量分布; 均聚物; 硬度高; 冲击性能好; High impact resistance,Wide molecular weight distribution,Good Hardness,Homopolymer
填料：碳酸钙
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.905 | g/cm³ | ASTM D792, ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
2.0 | g/10min | ASTM D1238，ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
1% 正割 1% secant 1 |
1500 | MPa | ASTM D638 |
|
-- -- |
1500 | MPa | ISO 527-2/1A/1 |
|
拉伸强度 tensile strength |
|||
|
屈服 yield 2 |
36.0 | MPa | ASTM D638 |
|
屈服 yield |
MPa | ISO 527-2/1A/50 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield 3 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/1A/50 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
J/m | ASTM D256-A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed 4 |
℃ | ISO 75-2/Bf | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed 5 |
℃ | ISO 75-2/Af | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
-- -- |
℃ | ASTM D1525, ISO 306/A 6 6 | |
|
-- -- |
℃ | ASTM D1525, ISO 306/B 7 7 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.039 in/min |
| 3 2.0 in/min |
| 4 testbar 80*10*4mm |
| 5 标准 B (120°C/h), 压 力1 (10N) |
| 6 标准 B (120°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部 
1~5月中国塑料制品出口1069亿元 同比增长22.1%
2017-06-13 据中国海关总署最新统计，今年前5个月，中国货物贸易进出口总值10.76万亿元人民币(下同)，比去年同期增长19.8%。其中，出口5.88万亿元，增长14.8%;进口4.88万亿元，增长26.5%;贸易顺差9940亿元，收窄21.1%。 5月份，中国进出口总值2.35万亿元，增长18.3%。其中，出口1.32万亿元，增长15.5%;进口1.03万亿元，增长22.1%;贸易顺差2816亿元，收窄3.4%。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付