| 牌号简介 About |
|---|
| Dow耐力HFDK-9253超高压是一种低密度、低垂度、交联聚乙烯，设计用于高压和超高压应用中的电力电缆绝缘，满足IEC 60840的要求。它具有以下重要优势。1。优异的热稳定性2。良好的挤压性能3。良好的热定型性能4。污染水平极低 DOW ENDURANCE™ HFDK-9253 EHV is a long-life, unfilled, crosslinkable, low density polyethylene insulation compound of extreme cleanliness developed especially for the insulation of power cables that employ high electrical stresses. DOW ENDURANCE HFDK-9253 EHV has been designed for cable production processes on horizontal vulcanization lines and for cables with thick insulation manufactured on standard catenary vulcanization lines. DOW ENDURANCE HFDK-9253 EHV has been designed with a non-migrating stabilizer providing high thermal stability, long term stability and optimum crosslinking behavior. It has an enhanced degree of scorch retardance for fine mesh filtering and long production run lengths during cable manufacture. DOW ENDURANCE HFDK-9253 EHV is recommended especially for the insulation of extra high voltage power transmission cables rated above 230 kV. Specifications Cables insulated with DOW ENDURANCE HFDK-9253 EHV, using sound commercial manufacturing practice, would be expected to meet the latest editions of the following specifications and regulations: IEC 62067 AEIC CS9 ANSI/ICEA: S-108-720 GB/T 22078 |
产品描述 Product Description
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.920 | g/cm³ | ASTM D792 |
|
湿度 humidity |
< 200 | ppm | 内部方法 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
20.0 | MPa | ASTM D638 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
500 | % | ASTM D638 |
|
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度的变化率 The rate of change in tensile strength |
|||
|
150℃，168 hr 150℃，168 hr |
< 25 | % | ASTM D638 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热固性 thermosetting |
IEC 60811-2-1 | ||
|
负荷下：200℃ Under load: 200 ℃ |
% | IEC 60811-2-1 | |
|
无负荷伸长率：200℃ Elongation without load: 200 ℃ |
% | IEC 60811-2-1 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
|||
|
23℃ 23℃ |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
ASTM D149 | ||
|
3.18 mm 3.18 mm 2 |
kV/mm | ASTM D149 | |
|
3.18 mm 3.18 mm 3 |
kV/mm | ASTM D149 | |
|
3.18 mm 3.18 mm 4 |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
|||
|
23℃ 23℃ |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
23℃ 23℃ |
ASTM D150 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.2 MPa |
|
【新闻资讯】查看全部
碳纤维加强复合资料等高强度轻量化新资料将成为热宠
2018-01-23 量化与安全性如何取舍?其实，两者可以兼得。但多年来，车企为了满足上述需求而陷入进退两难的尴尬境地：一部分车企注重轻量化(降低温室气体排放量)，另一部分车企注重车辆的安全性(采用较为厚重的部件，其做法与前者截然相反)。 2018年，新一代的材料应用速度将加快，这类材料重量更轻、安全性也更高，旨在同时满足愈发严苛的车辆安全性及二氧化碳排放量法规。铝材、高强度钢等材料将成为车辆的标配材料，碳纤维增强复合材料的强度及安全性更高，该材料目前被用于跑车中，未来将开始应用到更多其他类型的 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付