牌号简介 About |
---|
除了具有透明性、耐候性和机械强度的标准Sumipex外,Sumipex HT还具有更大的冲击强度。这种增强的强度功能可以减少成型或运输时可能发生的开裂量。 Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988- POM-K, M-GNR, 03-002, K5 POM copolymer Injection molding type, with special chalk modified; good wear properties; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation. UL-registration in natural and a thickness more than 1.57 mm as UL 94 HB, temperature index UL 746 B electrical 105 °C, mechanical 90 °C (tensile impact) and 80 °C (tensile). Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm. Ranges of applications: for unlubricated or once-only-lubricant sliding Parts. FMVSS = Federal Motor Vehicle Safety Standard (USA) UL = Underwriters Laboratories (USA) |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
3000 | MPa | ISO 527-2/1A/1 |
拉伸强度 tensile strength |
|||
屈服 yield |
60.0 | MPa | ISO 527-2/1A/50 |
拉伸应变 Tensile strain |
|||
屈服 yield |
8.0 | % | ISO 527-2/1A/50 |
标称拉伸断裂应变 Nominal tensile fracture strain |
22 | % | ISO 527-2/1A/50 |
拉伸蠕变模量 Tensile creep modulus |
ISO 899-1 | ||
1 hr 1 hr |
2500 | MPa | ISO 899-1 |
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature 3 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
cm³/10min | ISO 1133 | |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
Density of Melt Density of Melt |
g/cm³ | 内部方法 | |
Specific Heat Capacity of Melt Specific Heat Capacity of Melt |
J/kg/℃ | 内部方法 | |
Thermal Conductivity of Melt Thermal Conductivity of Melt |
W/m/K | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法 A |
3 VST 25±3, 4 hrs |
4 Method A |
5 60%, 1kHz |
【新闻资讯】查看全部
“绿发会”掀起智能制造风潮 展现江西智能工业魅力
2016-11-09 经党中央、国务院批准,由江西省人民政府主办的第四届世界绿色发展投资贸易博览会(以下简称“绿发会”)将于2016年11月25-28日在江西南昌召开!这标志着我国集展示世界绿色发展成就、全球生态文明建设成果、国际投资贸易合作成效的国际化开放平台正式落户江西。目前,以绿色发展和生态文明建设为主题的投资贸易博览会,“绿发会”在全国是第一个,也是唯一的,其意义相当于绿色发展的“B20峰会”。 绿发会以“绿色发展让世界更美好”为主题,将通过论坛研讨、展览展示、投资合作、贸易促进等方式, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |