牌号简介 About |
---|
PA 66,40%玻璃纤维,注塑成型,热老化稳定 Durethan® AKV40H2.0 901510 (Dry) PA 66, 40 % glass fibers, injection molding, heat-aging stabilized Durethan® AKV40H2.0 901510 PA 66, 40 % glass fibers, injection molding, heat-aging stabilized Durethan® AKV40H2.0 901510 PA 66, 40 % glass fibers, injection molding, heat-aging stabilized |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.46 | g/cm³ | |
收缩率 Shrinkage rate |
|||
TD:120℃,2.0 mm TD:120℃,2.0 mm |
0.050 | % | |
TD:290℃,2.0 mm TD:290℃,2.0 mm |
0.94 | % | |
MD:120℃,2.0 mm MD:120℃,2.0 mm |
0.050 | % | |
MD:290℃,2.0 mm MD:290℃,2.0 mm |
0.34 | % | |
TD:120℃,3.0 mm TD:120℃,3.0 mm |
% | ||
TD:290℃,3.0 mm TD:290℃,3.0 mm |
% | ||
MD:120℃,3.0 mm MD:120℃,3.0 mm |
% | ||
MD:290℃,3.0 mm MD:290℃,3.0 mm |
% | ||
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ||
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ||
拉伸蠕变模量 Tensile creep modulus |
|||
1 hr 1 hr |
MPa | ||
1000 hr 1000 hr |
MPa | ||
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ||
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ||
弯曲应变 Bending strain |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
维卡软化温度 Vicat Softening Temp |
℃ | ||
熔融温度 Melting temperature |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ||
TD:23~55℃ TD:23~55℃ |
1/℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ||
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ||
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | ||
相对电容率 Relative permittivity |
|||
23℃,100 Hz 23℃,100 Hz |
|||
23℃,1 MHz 23℃,1 MHz |
|||
耗散因数 Dissipation factor |
|||
23℃,100 Hz 23℃,100 Hz |
|||
23℃,1 MHz 23℃,1 MHz |
|||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.75 mm 0.75 mm |
|||
1.50 mm 1.50 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
|||
2.0 mm 2.0 mm |
℃ | ||
极限氧指数 Extreme oxygen index |
% | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
备注 |
---|
2. 60x60x2mm, 4 hr |
3. 60x60x2mm, 80°C MT, 600 bar |
4. 150x105x3mm, 4 hr |
5. 150x105x3mm, 80°C MT, 400 bar |
6. 2.0 mm/min |
7. 2 mm/min |
8. 10°C/min |
9. 程序 A |
【新闻资讯】查看全部
宁夏成立首个环境资源维护法庭剑指环保守法
2017-12-08 宁夏首个环境资源保护法庭――西夏区人民法院“贺兰山环境资源保护法庭”正式获准设立。此举将有利于更好地打击生态环保违法犯罪行为,维护宁夏六盘山、贺兰山、罗山的生态安全,有利于运用法律手段推进美丽宁夏建设。 据了解,新成立的“贺兰山环境资源保护法庭”将受理南至青铜峡市,北至石嘴山市大武口区地域范围内的各类环境保护案件。涉及环境资源类案件将全部集中审理,主要包括非法占用农用地、非法采矿、非法采伐、非法猎捕等各类违法犯罪行为。同时,这个法庭将依法审理旅游区内涉及旅游合同、旅游服务、 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |