Ultem 1000P树脂标准流聚醚酰亚胺(TG 217C),350微米粉末。符合生态要求。ultem 1000P树脂标准流量聚乙烯酰亚胺(TG 217C),350微米粉末。树脂符合RoHS标准。 Standard flow Polyetherimide (Tg 217C) in 350 micron powder. ECO Conforming. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.27 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
337℃,6.60kg 337℃,6.60kg |
9.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.50 to 0.70 | % | 内部方法 |
吸水率 Water absorption rate |
|||
平衡,23℃ Equilibrium, 23 ℃ |
1.3 | % | ASTM D570 |
24hr 24hr |
0.25 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D4812 | |
落锤冲击 Drop hammer impact |
|||
23℃ 23℃ |
J | ASTM D3029 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 5 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-20:150℃ TD:-20:150℃ |
1/℃ | ASTM E831 | |
MD:-20~150℃ MD:-20~150℃ |
1/℃ | ASTM E831 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
ASTM D149 | ||
1.6 mm,在空气中 1.6 mm in air |
kV/mm | ASTM D149 | |
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 kHz 1 kHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
2.45 GHz 2.45 GHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 3 |
|||
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 4 |
|||
100 mm跨距 100 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
|||
屈服,100 mm跨度 Yield, 100 mm span 4 |
MPa | ASTM D790 | |
泊松比 Poisson's ratio |
ASTM D638 | ||
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | ASTM D1044 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Tensile Bar |
3 0.20 in/min |
4 类型 1, 0.20 in/min |
5 0.10 in/min |
6 0.079 in/min |
7 Yield |
8 80*10*4 sp=62mm |
9 80*10*4 |
10 120*10*4 mm |
11 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
推动提高石化、化工、有色等行业绿色化水平
2021-03-26 搜料网资讯: 近日,国家发改委等13部门发布关于加快推动制造服务业高质量发展的意见。意见提出,在冶金、石化等重点领域遴选一批实施成效突出、复制推广价值大的智能制造标杆 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |