聚酰胺66中粘度30%玻璃纤维增强,阻燃剂UL94V0和5VA额定,热稳定,非常好的防火也在低厚度。高机械和热性能,低收缩和高尺寸稳定性,高跟踪电阻。UL94 V0所有颜色,0.75 mm和5 VA,1.5 mm-UL746 B批准-UL746 A CTI 1级,HAI 0级,HWI 0级标准AFNOR NF F 16-101和NF F 16-102 I2-F3批准用于2 mm黑色。提供:不同颜色。 Polyamide 66 medium viscosity 30% glass fibres reinforced, flame retardant UL94 V0 and 5VA rated, heat stabilized, very good flame proofing also at low thickness. High mechanical and thermal properties, low shrinkage and high dimensional stability, high tracking resistance. UL94 V0 all colours at 0.75 mm and 5VA at 1.5 mm-UL746 B approved-UL746 A CTI class 1, HAI class 0, HWI class 0-Norm AFNOR NF F 16-101 and NF F 16-102 class I2-F3 approved for Black color at 2 mm. Available: different colours. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.56 到 1.58 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
内部方法 | ||
TD TD |
0.45 到 0.75 | % | 内部方法 |
MD MD |
0.30 到 0.50 | % | 内部方法 |
吸水率 Water absorption rate |
ISO 62 | ||
23℃,24hr 23℃,24hr |
0.50 | % | ISO 62 |
饱和,23℃ Saturation, 23 ℃ |
4.5 | % | ISO 62 |
Granule Humidity Granule Humidity 3 |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 4 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 5 |
|||
1.8 MPa,未退火 1.8 MPa, unannealed 5 |
℃ | ISO 75-2/A | |
连续使用温度 Continuous use temperature 6 |
℃ | UL 746B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
球压测试 Ball pressure test |
|||
230℃ 230℃ |
IEC 60695-10-2 | ||
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-30~30℃ MD:-30~30℃ |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative temperature index |
UL 746 | ||
电气性能,0.75 mm Electrical performance, 0.75 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
0.75 mm 0.75 mm |
℃ | UL 746 | |
3.00 mm 3.00 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
2 mm 2 mm |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 | ||
解决方案 A Solution A |
V | IEC 60112 | |
解决方案 B Solution B |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
Reaction to Fire Reaction to Fire |
NF F 16-101/102 | ||
烟雾指数 Smoke index |
NF F 16-101/102 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灰份含量 Ash Content 7 |
|||
850℃ 850℃ 7 |
% | ISO 3451 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 TARO 002 |
3 0,039 in/min |
4 120°C/hr |
5 Short Term |
6 1 hr |
【新闻资讯】查看全部
美的收购东芝 最“受伤”的是谁?
2016-04-01 东芝退出家电业务,接盘者美的集团成为市场关注的焦点。这不会是日本家电业向中国输出品牌的最后一个并购案,中国家电业可能会成为日本家电产业的终结者。 中国家电业用强大的资本力量正在“吞噬”曾经盛极一时的日本家电产业。退出家电产业,不代表日本家电技术的完败,与中国家电业走到一起,保留日本家电原有的品牌,即是历史的追忆,也是消费者接受品牌的过渡期。 美的收购东芝,最受伤的是日本家电业。随着中国自主创新,新技术正成中国角逐国际市场的秘密武器。如果说过去几十年日本用新技 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |