牌号简介 About |
---|
5分钟固化的无下垂环氧树脂。这些高粘合强度粘合剂是透明的100%固体,双组分,无下垂粘合剂,在室温下快速固化5-46分钟。适用于电镀金属、白镴、玻璃、木材、陶瓷、毛毡、水泥、宝石、大多数塑料和橡胶等的粘合。这些粘合剂在我们实验室进行了阻燃性能测试。根据我们的测试结果,它们符合UL94HB的要求。应用:这些独特的粘合剂非常适合广泛的电子、电气、工业、结构和珠宝应用。这些粘合剂也是现场维修的最佳选择。它们在流行的Triggerbond双筒药筒分配系统和散装包装中提供。特点:无下垂度,高粘结强度,室温快速固化,三种速度可选,耐水性和耐化学性优异,抗热震性1:1配合比,抗冲击性强。 5 MINUTE SET NON-SAG EPOXY These high bond strength adhesives are clear 100% solids, two component, non-sag adhesives with a quick setting time of 5-46 minutes at room temperature. They are excellent for bonding plated metals, pewter, glass, wood, ceramic, felt, cement, gem stones, most plastics and rubbers, etc... These adhesives were tested in our laboratory for flame retardancy properties. According to our test results they meet the requirements of UL94HB. Applications: These unique adhesives are ideally suited for a wide range of electronic, electrical, industrial, structural, and jewelry applications. These adhesives are also an excellent choice for field repairs. They are offered in the popular TriggerBond® dual barrel cartridge dispensing system and bulk packaging. Features: Non-sag consistency High bond strength Fast room temperature cure - three speeds to choose from Water & chemical resistance Outstanding thermal shock resistance 1:1 mix ratio Impact resistance |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
140 | J/m | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
6.0E-5 | 1/℃ | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Handle Time(25℃) Handle Time(25℃) |
15.0 到 20.0 | min | |
工作温度 working temperature |
-50.0 到 130 | ℃ | |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
Clear/Transparent | ||
重量混合比(PBW) Weight Mix Ratio (PBW) |
|||
Part A Part A |
|||
Part B Part B |
|||
体积混合比(PBV) Volume Mixing Ratio (PBV) |
|||
Part A Part A |
|||
Part B Part B |
|||
固体含量 Solid content |
% | ||
密度 Density |
|||
25℃ 25℃ |
g/cm³ | ||
固化时间 Curing time |
|||
25℃ 25℃ |
hr | ||
储存稳定性 storage stability |
|||
25 ℃ 25 ℃ |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
|||
压缩强度 compressive strength |
MPa | ||
耐电强度 Electrical strength |
kV/mm | ||
相对电容率 Relative permittivity |
|||
1 kHz,25℃ 1 kHz,25℃ |
|||
体积电阻率 Volume resistivity |
|||
25 ℃ 25 ℃ |
ohms·cm | ||
耗散因数 Dissipation factor |
|||
1 kHz 1 kHz |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
单原子超稳低汞催化剂完成产业化使用
2019-02-19 2月15日,记者从浙江工业大学了解到,由该校工业催化研究所自主研发的单原子超稳低汞催化剂已在河南神马氯碱万吨级装置上实现产业化应用。 该装置工业运行情况稳定,在吨耗、转化率、选择性及使用寿命上均具有明显优势,产品各项指标完全符合低汞触媒国家标准《GB/T31530-2015 氯乙烯合成用低汞触媒》的要求,为氯碱行业节能减排提供了有力的技术支撑。 催化剂在工业使用过程中理论上并不会消耗,涉汞催化剂的汞污染问题本质上是由于催化剂的热稳定性不好造成的。浙江工业大学 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |