牌号简介 About |
---|
高热量,低光泽,中等冲击的ABS树脂注塑应用:汽车内饰应用需要低挥发性有机化合物(VOC)。 High Heat, Low Gloss, Medium Impact ABS resin for injection molding Applications: Automotive interior trim applications requiring low volatile organic compounds (VOC). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.06 | g/cm³ | ASTM D792 |
密度 Density |
1.06 | g/cm³ | ISO 1183/B |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,3.80kg 230℃,3.80kg |
2.1 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
TD TD |
0.56 | % | ASTM D955 |
MD MD |
0.57 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength 2 |
|||
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 2 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus 4 , 5 |
MPa | ISO 178 | |
弯曲强度 bending strength 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 , 5 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-A | |
23℃ 23℃ |
kJ/m² | ISO 180-A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
-30℃,Peak Energy -30℃,Peak Energy |
J | ASTM D3763 | |
23℃,Peak Energy 23℃,Peak Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 6 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~100℃ TD:-40~100℃ |
1/℃ | ASTM E831 | |
MD:-40~100℃ MD:-40~100℃ |
1/℃ | ASTM E831 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
FMVSS Flammability FMVSS Flammability 7 |
mm/min | FMVSS 302 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 方法 I (三点负荷), 0.079 in/min |
4 0.079 in/min |
5 3 点 |
6 速率 A (50°C/h), 载荷2 (50N) |
7 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
【新闻资讯】查看全部
新型SIS材料如何助您制造高端卫生用品?
2022-01-18 搜料网资讯: 全球塑料膜市场以5%的年增长率稳定成长,其中包装膜类的应用最广,约占64%,包括食品包装、物品包装及收缩膜包装。医疗膜的应用则占6%左右,包括输液袋、医疗用手套 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |