| 牌号简介 About |
|---|
| JPPCABSI工程树脂旨在提供冲击强度、耐热性和加工性能之间的平衡。它提供了比聚碳酸酯更好的加工性能，同时在室温和低温下提供了比ABS高的冲击强度。JPPCABSI在230°F的负载（264 psi，未调节）下的偏转温度，与ABS相比，还具有较高的耐热性。JPPCABSI工程树脂已用于汽车仪表板和内饰应用。 JPPCABSI engineering resin is designed to offer a balance of properties between impact strength, heat resistance and processability. It offers better processability than polycarbonate while offering high impact strength at both room and low temperatures compared to ABS. With a deflection temperature under load (264 psi, unannealed) of 230°F, JPPCABSI also offers high heat resistance compared to ABS. JPPCABSI engineering resin has been used in automotive instrument panel and interior trim applications. |
产品描述 Product Description
加工条件：共挤出成型
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.13 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，3.80kg 230℃，3.80kg |
3.0 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.70 | % | ASTM D955 |
|
吸水率 Water absorption rate |
ASTM D570 | ||
|
23℃，24hr 23℃，24hr |
0.15 | % | ASTM D570 |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
0.32 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 2 |
ASTM D256 | ||
|
-40℃，3.2mm -40℃，3.2mm |
J/m | ASTM D256 | |
|
-30℃，3.2mm -30℃，3.2mm |
J/m | ASTM D256 | |
|
23℃，3.2mm 23℃，3.2mm |
J/m | ASTM D256 | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 3 |
ASTM D3763 | ||
|
-29℃，3.18 mm，Total Energy -29℃，3.18 mm，Total Energy |
J | ASTM D3763 | |
|
23℃，3.18 mm，Total Energy 23℃，3.18 mm，Total Energy |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
ASTM D648 | ||
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，退火，3.18 mm 1.8 MPa, annealed, 3.18 mm |
℃ | ASTM D648 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：-40~82℃ MD：-40~82℃ |
1/℃ | ASTM D696 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸强度 tensile strength 1 |
ASTM D638 | ||
|
屈服 yield |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain 1 |
|||
|
断裂 fracture 1 |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
|||
|
屈服 yield |
MPa | ASTM D790 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 类型 1, 2.0 in/min |
| 3 10 mil 缺口深度 |
| 4 11.1 ft/sec |
|
【新闻资讯】查看全部 
塑博会15个合作项目签约 8个项目投资均超10亿
2021-09-21 搜料网资讯： 11月6日，第十八届中国博览会招商推介会暨项目签约仪式举行，市领导奚明、卢建国、郑利刚出席。 市委副书记、市长奚明在推介会上致辞。他说，当前余姚正处于转型发 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付