| D/W 212是一种用纯聚四氟乙烯（PTFE）刮削而成的薄膜，该薄膜一面用萘钠蚀刻。这种表面处理可以使聚四氟乙烯（通常表现出很差的粘附力）与其他材料结合。钠蚀聚四氟乙烯的主要应用包括与弹性体粘合以生产层压隔膜，以及在聚四氟乙烯压敏带生产中应用压敏粘合剂。在上述所有应用中，层压或粘合应用通常通过特定于所应用材料的底漆完成。 D/W 212 is a film , skived from virgin PTFE, that has been etched on one side with sodium naphthalene. This surface treatment allows PTFE, which normally exhibits very poor adhesion, to be bonded to other materials. The major applications for sodium etched PTFE involve bonding to elastomers to produce laminated diaphragms, as well as the application of pressure sensitive adhesives in the production of PTFE pressure sensitive tapes. In all the above applications, the lamination or adhesive application is usually accomplished with a primer that is specific to the material being applied. |
产品描述 Product Description
用途：隔膜;薄膜;带子;粘合剂;
颜色：白色,自然色,黑色,红色
性能特点： 粘结性好; Good bond
填料：PTFE
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Thickness Thickness |
50.8 到 1020 | nm | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
MD，屈服 MD, yield |
27.6 | MPa | ASTM D882 |
|
拉伸应变 Tensile strain |
|||
|
MD，断裂 MD, fracture |
300 | % | ASTM D882 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
连续使用温度 Continuous use temperature |
260 | ℃ | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Core ID Core ID |
7.62 | cm | |
|
Maximum Roll OD Maximum Roll OD |
mm | ||
|
Width Width |
mm | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
瓦克嘉奖开发有机硅部件生产用三维打印新技术人员
2021-09-20 搜料网资讯： 慕尼黑，2016年10月20日瓦克化学股份有限公司昨天将亚历山大瓦克创新奖颁予Frank Achenbach博士、Bernd Pachaly博士、Maximilian ter博士和Ernst Selbertinger博士，表彰他们成功开发有 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付