牌号简介 About |
---|
QC-8744FR是一种低密度乙烯基酯基片状模塑料(SMC)。它设计用于需要结构强度、耐腐蚀性和耐温性以及低成型密度的部件的压缩成型。它具有很高的阻燃性,能满足低壁厚条件下的关键要求。 QC-8744FR is a low-density vinyl ester based sheet molding compound (SMC). It is designed for compression molding of components requiring structural strength, corrosion resistance and temperature resistance combined with low molded density. It is highly flame retarded to meet critical requirements at low wall thickness. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.32 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.050 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.15 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
138 | MPa | ASTM D638 |
弯曲模量 Bending modulus |
10300 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
3.20 mm 3.20 mm |
UL 94 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
贮藏期限 Storage period |
|||
24℃ 24℃ |
wk | ||
脱模时间 stripping time |
|||
149℃ 149℃ |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
打破国外垄断 拟出资2.7亿元 齐翔腾达与中化集团组建PA66产业基地 规划
2019-07-31 齐翔腾达7月25日晚间公告,公司近期与中国化学集团工程有限公司及其孙公司中国天辰工程有限公司就共同投资建设生产高新材料尼龙66(PA66)达成一致,发起设立天辰齐翔新材料有限 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |