牌号简介 About |
---|
Riblene® FF 34是一种高分子量低密度聚乙烯(LDPE),加入滑脱和防堵剂,适用于吹塑薄膜挤出。Riblene® FF 34的特点是具有良好的熔融强度,在由Riblene® FF 34制造的挤出薄膜中具有良好的气泡稳定性,易于热收缩,具有良好的机械性能。主要应用Riblene® FF 34推荐用于一般包装膜、购物者、层压膜和混合膜的生产。 Riblene FF 34 is a high molecular weight low density polyethylene (LDPE), additivated with slip and antiblocking agent, suitable for blown film extrusion. Riblene FF 34 is characterised by a good melt strength leading to a good bubble stability during extrusion Films manufactured by Riblene FF 34 are easily heat shrinkable and characterised by good mechanical properties. Main Application Riblene FF 34 is recommended for the production of general packaging film, shoppers, lamination film and blend. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.923 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.75 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态,吹塑薄膜 Self dynamic, blow molded film |
0.15 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
70 | µm | |
薄膜厚度 film thickness |
30 to 120 µm | ||
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,70 µm,吹塑薄膜 1% secant, MD, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
1% 正割,TD,70 µm,吹塑薄膜 1% secant, TD, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,70 µm,吹塑薄膜 MD, yield, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,70 µm,吹塑薄膜 TD, yield, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,70 µm,吹塑薄膜 MD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,70 µm,吹塑薄膜 TD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,70 µm,吹塑薄膜 MD, fracture, 70 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,70 µm,吹塑薄膜 TD, fracture, 70 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact 2 |
|||
70 µm,吹塑薄膜 70 µ m, blow molded film 2 |
g | ISO 7765-1/A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ISO 6383-2 | ||
MD:70.0 µm MD:70.0 µm |
kN/m | ISO 6383-2 | |
TD:70.0 µm TD:70.0 µm |
kN/m | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,70 µm,吹塑薄膜 45 °, 70 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
70.0 µm,吹塑薄膜 70.0 µ m, blow molded film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
3 Blown Film |
【新闻资讯】查看全部
华北地域供暖季,苯乙烯市场产生繁重压力
2018-10-23 根据生态环境部发布的《京津冀及周边地区2018-2019年秋冬季大气污染综合治理攻坚行动方案》(以下简称《方案》)来看,今年华北地区的供暖季,依然将对苯乙烯市场产生沉重压力。 《方案》的实施范围包括:北京市,天津市,河北省石家庄、唐山、邯郸、邢台、保定、沧州、廊坊、衡水市,山西省太原、阳泉、长治、晋城市,山东省济南、淄博、济宁、德州、聊城、滨州、菏泽市,河南省郑州、开封、安阳、鹤壁、新乡、焦作、濮阳市,基本覆盖了整个北方苯乙烯市场。 《方案》中,对苯乙烯影响 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |