| 牌号简介 About |
|---|
| SABIC® PP QR675K是一种高度透明的无规共聚物，具有良好的抗静电性能和良好的流动性。这一等级结合了改进的美学成品和低温加工能力。部件美观性不受较低温度的影响，从而提供更宽的操作窗口。SABIC® PP QR675K具有优良的脱模特性，具有良好的刚度与冲击比。SABIC® PP QR675K主要用于注塑工艺。SABIC® PP QR675K的目标是透明的应用是更高的MFI的良好流动性是必需的。它的预期应用包括注塑家庭用品，办公室和家庭存储盒，薄壁包装和媒体包装。本文所述产品尤其未经测试，因此未经验证可用于医药/医疗应用。 SABIC® PP QR675K is a highly transparent random copolymer with good antistatic properties with excellent flow behaviour. This grade combines improved aesthetics of the finished articles with low temperature processability. Part aesthetics are not affected by the lower temperatures, providing for a broader operating window. The SABIC® PP QR675K results in excellent demoulding characteristics and has a good stiffness to impact ratio. SABIC® PP QR675K is mainly used in injection moulding processes. The SABIC® PP QR675K aims at transparent applications were higher MFI's with good flow are required. Its intended applications include injection moulded housewares, office & home storage boxes, thin wall packaging and media packaging. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
产品描述 Product Description
用途：透明零件;家用货品;容器;媒介包装;薄壁包装;
颜色：清晰/透明
加工条件：注射成型 Injection Molding
性能特点： 抗静电; 机械强度好; 含脱模剂; 透光性好; 流动性高; 无规共聚物; 冲击性能好; 表面光泽度好; Good Rigidity,Good Clarity,Good surface appearance,High impact resistance,High liquidity,Good stripping performance,Random copolymer,Antistatic property
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.905 | g/cm³ | ASTM D792, ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
60 | g/10min | ASTM D1238，ISO 1133 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
0℃ 0℃ |
2.0 | kJ/m² | |
|
23℃ 23℃ |
4.5 | kJ/m² | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
0℃ 0℃ |
30 | J/m | ASTM D256-A |
|
23℃ 23℃ |
J/m | ASTM D256-A | |
|
0℃ 0℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed 4 |
℃ | ISO 75-2/Bf | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed 5 |
℃ | ISO 75-2/Af | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
-- -- |
℃ | ASTM D1525，ISO 306/A120 6 6 | |
|
B120 B120 |
℃ | ASTM D1525, ISO 306/B120 7 7 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
雾度 Haze |
% | ASTM D1003 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ISO 868 | ||
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
|||
|
1% 正割 1% secant 1 |
MPa | ASTM D638 | |
|
-- -- |
MPa | ISO 527-2/1A/1 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield 2 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/1A/50 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield 3 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/1A/50 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.039 in/min |
| 3 2.0 in/min |
| 4 testbar 80*10*4mm |
| 5 标准 B (120°C/h), 压 力1 (10N) |
| 6 标准 B (120°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部
我国首条千吨级T800碳纤维消费线投产
2017-10-10 我国首条千吨级T800碳纤维10号生产线，9月29日在连云港开发区中复神鹰碳纤维有限公司正式投产运行，标志着我国高端碳纤维产业化实现新突破。 据中国建材董事长宋志平介绍，中复神鹰T800碳纤维10号线是目前国内最先进的碳纤维生产线，年产能为1000吨，在全线自动化程度、绿色环保生产、废气治理等方面均达到国内领先水平，性能指标赶超国外同类产品水平，可完全替代进口，实现我国T800碳纤维产品自给自足。 碳纤维属于高性能新型纤维材料，广泛用于航天航空、军工、交通、 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付