牌号简介 About |
---|
EpoxAcast® 670 HT(以前为20-136)是一种环氧浇注化合物,如果使用后固化计划,其耐热性高达350°F/177°C。EpoxAcast® 670 HT具有相对较低的粘度,确保最小的气泡截留。EpoxAcast® 670 HT还提供3小时的超长工作时间。铸件的固化可以忽略收缩,非常坚硬、非常坚固和耐热。EpoxAcast® 670 HT是制造真空模具,铸造模式,成型模具和夹具,硬辊,工业零件和高冲击工具的理想选择。EpoxAcast® 670 HT也适用于封装应用或用作高温环氧树脂,用于粘合各种表面。 EpoxAcast® 670 HT (formerly 20-136) is an epoxy casting compound which offers high heat resistance up to 350° F/177° C if post cure schedule is used. EpoxAcast® 670 HT features a relatively low viscosity that ensures minimal bubble entrapment. EpoxAcast® 670 HT also offers an extra long working time of 3 hours. Castings cure with negligible shrinkage and are very hard, very strong and heat resistant. EpoxAcast® 670 HT is ideal for making vacuum form molds, foundry patterns, forming dies & fixtures, hard rollers, industrial parts and high impact tools. EpoxAcast® 670 HT is also suitable for encapsulation applications or for use as a high temperature epoxy for bonding a variety of surfaces. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.15 | g/cm³ | ASTM D1475 |
特定体积 Specific volume |
0.741 | cm³/g | ASTM D792 |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time 4 |
1.0 | day | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
90 | ASTM D2240 | |
拉伸模量 Tensile modulus |
2290 | MPa | ASTM D638 |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed 2 |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed 3 |
℃ | ASTM D648 | |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
|||
储存稳定性 storage stability |
min | ASTM D2471 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 if post cured according to heat curing schedule |
3 If cured at room temperature |
4 followed by: Heat cure for 2 hrs at 175°F/80°C followed by 3 hrs at 300°F/150°C |
【新闻资讯】查看全部
大连商品交易所29日PP行情表
2021-12-30 搜料网资讯: 大连商品交易所 日行情表 查询日期: 20 21 年 12 月 29 日 本月第 21 个交易日 本年第 241 个交易日 商品 交割月份 开盘价 最高价 最低价 收盘价 前结算价 结算价 涨跌 涨跌 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |