| 牌号简介 About |
|---|
| Lumicene MPE M 3410 EP是以己烯为共聚单体的第二代茂金属基中密度聚乙烯。与传统的LLDPE和第一代茂金属聚乙烯相比，鲁米新MPE M 3410 EP的挤出压力低、气泡稳定性好、表观控制能力强，产量高。这些特征的结合带来了显著的下调潜力。Lumicene MPE M 3410 EP特别适用于需要高光泽和高透明度的薄膜应用，特别是在混合和与LLDPE或LDPE共挤时。Lumicene MPE M 3410 EP适用于消费者、工业、食品或卫生包装领域的许多应用，如整理收缩、邮寄膜、重型袋、袋、层压和卫生膜。 Lumicene® mPE M 3410 EP is a second generation metallocene based Medium Density Polyethylene with hexene as comonomer. Lumicene® mPE M 3410 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The combination of these features brings a significant downgauging potential. Lumicene® mPE M 3410 EP is especially dedicated to film applications where high gloss and high transparency are required, particularly in blend and in coextrusion with LLDPE or LDPE. Lumicene® mPE M 3410 EP is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as collation shrink, mailing film, heavy-duty sacks, bags, lamination and hygiene film. |
产品描述 Product Description
用途：重包装袋;薄膜;包装;袋子;收缩性薄膜;食品包装;层压板;吹膜;混合;
加工条件：吹塑薄膜
性能特点： 抗氧化; 透光性好; 己烯共聚单体; 良好的测量控制; 表面光泽度好; Good Clarity,Good surface appearance,Good Gauge Control,Inoxidizability,Hexene copolymers
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.934 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.90 | g/10min | ISO 1133 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
40 | µm | |
|
拉伸强度 tensile strength |
|||
|
MD，屈服，40 µm，吹塑薄膜 MD, yield, 40 µ m, blow molded film |
17.0 | MPa | |
|
TD，屈服，40 µm，吹塑薄膜 TD, yield, 40 µ m, blow molded film |
18.0 | MPa | |
|
MD，断裂，40 µm，吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ||
|
TD，断裂，40 µm，吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
MPa | ||
|
拉伸应变 Tensile strain |
|||
|
MD，断裂，40 µm，吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ||
|
TD，断裂，40 µm，吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ||
|
落锤冲击 Drop hammer impact |
|||
|
40 µm，吹塑薄膜 40 µ m, blow molded film |
g | ISO 7765-1 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
|
MD：40 µm，吹塑薄膜 MD: 40 µ m, blow molded film |
N | ||
|
TD：40 µm，吹塑薄膜 TD: 40 µ m, blow molded film |
N | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，40.0 µm，吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
40 µm，吹塑薄膜 40 µ m, blow molded film |
% | ISO 14782 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Blown Film Melt Temperature Blown Film Melt Temperature |
|||
| 备注 | |||
|---|---|---|---|
| 暂无数据 | |||
|
【新闻资讯】查看全部
因透明而撩人的PC使用于哪四个范畴？
2017-02-10 在材料界，有很多很多完全透明材料，但是要说到兼备完美韧性及实用性的塑料材料，那非PC莫属了。PC又称聚碳酸酯，也是产品中常用的一种塑料材质，它经常用来代替玻璃，特别是在生产酒瓶酒杯等类似制品时，很多商家为了降低玻璃易碎的这种风险性就会直接用PC来作为主材料大规模生产。 PC塑胶粒不能长期接触60℃以上的热水，PC燃烧时会发出热解气体，塑料烧焦起泡，但不着火，离火源即熄灭，发出稀有薄的苯酚气味，火焰呈黄色，发光淡乌黑色，温度达140℃开始软化，220℃熔解，可吸红外线光谱。< |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名：搜料网-TOTAL Polyethylene Lumicene® M 3410 EP (EU - Blown Film)证书
发送至：（多个地址，中间以逗号隔开）
发送一份副本给我：您还没有填写邮箱!(点击完善资料)
当前牌号已加入对比
支付宝
微信支付