牌号简介 About |
---|
高密度聚乙烯用于制造大桶、漂白瓶、购物袋、板条箱、网和桶。强硬的。僵硬的重型的。具有很高的耐化学性。这些品质使聚乙烯适合于各种工业产品。吹塑薄膜:购物袋和杂货袋管道:压力和非压力管道吹塑:家用和工业化学品瓶,大桶注射成型:托盘、板条箱、箱子、托盘、玩具、家居用品、盖子 EVALENE ® HF09522 is ideal for stiff and strong films. Bags made of EVALENE ® HF09522 can carry heavy loads and exhibit good puncture resistance. Packaging made from EVALENE ® HF09522 has superior performance and good barrier resistance against moisture and oxygen. Downgauging using EVALENE ® HF09522 is highly recommended due to its superior mechanical properties. Optimum gauge reduction is a real possibility. FEATURES Superior toughness High stiffness Good puncture resistance Good moisture barrier properties Meets FDA Philippines food-contact requirements Halal certified TYPICAL APPLICATIONS FEATURES Grocery bags Supermarket produce bags Carrier bags Trash bags Sack liners |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
0.952 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg 3 |
0.075 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
9.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
割线模量 Secant modulus 4 |
ASTM D882 | ||
1% 正割,MD:25 µm 1% secant, MD: 25 µ m |
786 | MPa | ASTM D882 |
1% 正割,TD:25 µm 1% secant, TD: 25 µ m |
MPa | ASTM D882 | |
拉伸强度 tensile strength 5 |
ASTM D882 | ||
MD,屈服,25 µm MD, yield, 25 µ m |
MPa | ASTM D882 | |
TD,屈服,25 µm TD, yield, 25 µ m |
MPa | ASTM D882 | |
MD,断裂,25 µm MD, fracture, 25 µ m |
MPa | ASTM D882 | |
TD,断裂,25 µm TD, fracture, 25 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain 5 |
ASTM D882 | ||
MD,屈服,25 µm MD, yield, 25 µ m |
% | ASTM D882 | |
TD,屈服,25 µm TD, yield, 25 µ m |
% | ASTM D882 | |
MD,断裂,25 µm MD, fracture, 25 µ m |
% | ASTM D882 | |
TD,断裂,25 µm TD, fracture, 25 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
25 µm 25 µm |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:25 µm MD:25 µm |
g | ASTM D1922 | |
TD:25 µm TD:25 µm |
g | ASTM D1922 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blow(up Ratio) Blow(up Ratio) |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Product is controlled by Flow Index. melt Index is estimated for customer use. |
3 0.98 in/min |
4 20 in/min |
【新闻资讯】查看全部
中国高通明聚丙烯初次出口日本
2017-09-20 日前,宁波梅山保税港区,STAR SKIPPER号远洋货船鸣笛起航,镇海炼化12吨透明聚丙烯M26ET发往日本。这不仅是中国石化高透明聚丙烯产品首次出口日本,也是中国高透明聚丙烯产品首次打入日本市场,为聚丙烯产品大步“走出去”奠定坚实基础。 2014年11月,镇海炼化高端产品透明聚丙烯M26ET研发成功,熔指达到26克/10分钟,突破了当时国产环管工艺聚丙烯无规共聚牌号的熔指上限。独特的加工工艺使该产品具有极高的硬度、刚性和透明度。产品主要应用于注塑包装和吹塑成型等加工领域 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |