牌号简介 About |
---|
TC-1600 A/B是一种未填充的低粘度层压树脂,通常用于制造增强层压板。它具有在室温下固化的能力,适用于不需要工作温度高于180°F(82°C)的应用。该系统可在后固化时提供高达300°F(149°C)的服务。TC-1600通常用于加固玻璃纤维、芳纶/芳纶和碳纤维织物。它还用作粘合木材、复合材料和其他基材的粘合剂。添加填充剂,如气相二氧化硅,微球和短链纤维,可以创建填充剂,整流罩和粘合应用的糊状物。 TC-1600 A/B is an unfilled, low viscosity laminating epoxy resin for variety of fabricating applications. It features the ability to cure at room temperature for applications that do not require a working service temperature above 180°F (82?C). When post cured at elevated temperatures, this system can provide service up to 300°F (149°C). TC-1600 is commonly used to reinforce fiberglass, Kevlar/aramid, and carbon fiber fabrics. It is also used as an adhesive for bonding wood, composites, and other substrates. Adding fillers like fumed silica, micro-spheres, and short-strand fibers can create pastes for fillets, fairings, and bonding applications. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
270 | J/m | ASTM D256 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
95 | ASTM D2240 | |
拉伸强度 tensile strength |
|||
屈服 yield |
241 | MPa | ASTM D638 |
弯曲模量 Bending modulus |
15900 | MPa | ASTM D790 |
弯曲强度 bending strength |
276 | MPa | ASTM D790 |
压缩强度 compressive strength |
MPa | ASTM D695 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
密度 Density |
|||
Part A:25℃ Part A:25℃ |
g/cm³ | ||
Part B:25℃ Part B:25℃ |
g/cm³ | ||
吸水率 Water absorption rate |
|||
100hr 100hr |
% | ASTM D570 | |
收缩率 Shrinkage rate |
% | ||
布络克菲尔德粘度 Brookfield viscosity |
|||
混合,25℃ Mixing, 25 ℃ |
Pa·s | ||
Part A,25℃ Part A,25℃ |
Pa·s | ||
Part B,25℃ Part B,25℃ |
Pa·s | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D3386 | |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
|||
后固化时间 Post curing time |
hr | ||
脱模时间 stripping time |
|||
25℃ 25℃ |
hr | ||
工作时间 working hours 1 |
|||
25℃ 25℃ 1 |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 1 lb mass |
【新闻资讯】查看全部
海关总署:2016前2月塑料制品出口下降11%
2016-03-23 记者从海关总署处了解到,2016年前2个月,我国进出口总值比去年同期下降12.6%,其中,塑料制品349.5亿元,下降11%;初级形状的塑料361万吨,减少4.7%,进口均价为每吨1.02万元,下跌6.4%。 据统计,我国进出口总值3.31万亿元人民币,比去年同期(下同)下降12.6%。其中,出口1.96万亿元,下降13.1%;进口1.35万亿元,下降11.8%;贸易顺差6159亿元,收窄15.9%。2月份,我国进出口总值1.43万亿元,下降15.7%。其中,出口8218亿 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |