| 牌号简介 About |
|---|
| Alcudia 5502-E天然化合物是一种中等分子量的己烯共聚物，适用于电缆、单层或多层电缆保护波纹管的挤出。本产品为天然色，但在加工温度下稳定的颜料可轻易着色，采用干着色或母料技术，Alcudia 5502E是一种高分子量的高密度聚乙烯己烯共聚物。它是专门设计，通过吹塑挤出，液体洗涤剂和化学品罐。该等级包含根据物品最终用途的稳定剂，以增强热稳定性。由于Alcudia5502E分子量和密度的关系，它具有良好的抗环境应力开裂性能。非腐蚀性液体洗涤剂和化学品的典型应用包装。推荐的熔化温度范围为180至200°C。应为每条生产线优化加工条件。 ALCUDIA® 5502-E natural compound is an hexene copolymer of medium molecular weight apt for the extrusion of corrugated pipes for protection of cables, one or multilayered pipe. This product is supplied in natural colour but it can be easily coloured with pigments steady at processing temperature, using dry-colouring or masterbatch techniques ALCUDIA® 5502E is a high-density polyethylene copolymer of hexene, with high molecular weight. It is specially designed to make, by blow molding-extrusion, tanks for liquid detergents and chemicals. This grade contains stabilizers according to the end use of the item in order to reinforce the thermal stability. Good environmental stress cracking resistance can be obtained with ALCUDIA® 5502E due to its molecular weight and density. TYPICAL APPLICATIONS Packaging of non-aggressive liquid detergents and chemicals. Recommended melt temperature range from 180 to 200°C. Processing conditions should be optimised for each production line. |
产品描述 Product Description
用途：管道系统;
颜色：黑色
加工条件：管路挤出成型
性能特点： 抗氧化; 高分子量; 己烯共聚单体; 食品接触; 抗应力开裂; Food contact compliance,Inoxidizability,High molecular weight,Hexene copolymers,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.954 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
|
190℃，2.16kg 190℃，2.16kg |
0.11 | g/10min | ISO 1133 |
|
190℃，21.6kg 190℃，21.6kg |
11 | g/10min | ISO 1133 |
|
190℃，5.0kg 190℃，5.0kg |
0.50 | g/10min | ISO 1133 |
|
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
|
10%乳化剂，F50 10% emulsifier, F50 |
> 1000 | hr | ASTM D1693 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ISO 868 | ||
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | EN 638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | EN 638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
内部压力阻力 Internal pressure resistance |
EN 1555/12201 | ||
|
10 MPa：20℃ 10 MPa：20℃ |
day | EN 1555/12201 | |
|
4.0 MPa：80℃ 4.0 MPa：80℃ |
day | EN 1555/12201 | |
|
4.6 MPa：80℃ 4.6 MPa：80℃ |
day | EN 1555/12201 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
|
氧感应时间 Oxygen sensing time |
|||
|
210℃ 210℃ |
min | EN 728 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Long-Term Hydrostatic Strength - 50 years（20℃） Long-Term Hydrostatic Strength - 50 years（20℃） 3 |
MPa | ISO TR 9080 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 速率 A (50°C/h) |
| 3 Regression Curve |
|
【新闻资讯】查看全部
中石油独石化年产乙烯132.15万吨 产量蝉联全国第一
2018-02-07 记者从中国石油天然气集团有限公司获悉，独山子石化公司2017年生产乙烯132.15万吨，比上年增产1.35万吨，再创历史新高，蝉联全国第一。 乙烯是石油化工的基础性原料，被誉为“石化之母”。据中国报告网披露，2017年全球乙烯产量1.5197亿吨，独山子石化的产量占全球的0.87%，是全国乙烯产量最高的石化企业。独山子石化2016年乙烯产量达到130.8万吨，居全国第一，2017年生产乙烯132.15万吨，再创新高。 据介绍，2017年，独山子石化公司努力实 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |