| 牌号简介 About |
|---|
| 矿物充填级，翘曲度低，易流动，表面光滑。根据ISO 1043-1的化学缩写：LCP固有阻燃塞拉尼斯已在FDA建立了Vectra® MT4350的药物主文件（DMF 8468）和设备主文件（MAF 315）。这些是为了帮助我们的客户最终使用FDA的申请。Vectra® MT4350已经过测试，并符合美国药典第六类。 Vectra® MT4350 VF3001 (natural) is a mineral filled high flow LCP grade for injection molding Vectra MT4350 VF3001 (natural) is a special grade developed for medical industry applications and complies with: Food Contact Substance Notification (FCN) No. 742 of the Food and Drug Administration (FDA) and is listed in the Drug Master File (DMF 8464) and the Device Master File (MAF 315) the corresponding EU and national registry regulatory requirements biocompatibility in tests corresponding to USP 23 Class VI and/or ISO 10993 low residual monomers no animal products Mineral filled grade with low warp, easy flow and smooth surface appearance. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant |
产品描述 Product Description
性能特点： 防火阻燃等级V-0; 低翘曲性; 易流动; 表面光泽度好; Low warping,Good surface appearance,Good liquidity,V-0
填料：矿物 40
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.74 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage rate |
ISO 294-4 | ||
|
TD TD |
0.50 | % | ISO 294-4 |
|
MD MD |
0.0 | % | ISO 294-4 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
9800 | MPa | ISO 527-2/1A/1 |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
105 | MPa | ISO 527-2/1A/5 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2/1A/5 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD TD |
1/℃ | ISO 11359-2 | |
|
MD MD |
1/℃ | ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
相对电容率 Relative permittivity |
|||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
|||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
1.50 mm 1.50 mm |
UL 94 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 10°C/min |
|
【新闻资讯】查看全部 
逐鹿中原！伊之密将携ECO高速注坯零碎亮相郑州塑博会
2017-02-27 近年来，河南省塑料制品行业高速增长，其中日用塑料制品在2016年1-11月份累计产量24.6049万吨，同比增幅30.22%，领跑全国市场，尤其饮料、粮油等PET包装行业发展较为迅猛。 为满足河南市场的需 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付