| 牌号简介 About |
|---|
| 用13%的玻璃纤维进行化学增强，适用于在负温度下具有高强度和韧性的塑件。用于汽车、工程和电气行业。随着fg含量的增加，材料的韧性、拉伸强度和弯曲强度增加，收缩率降低，热处理温度提高到250°C，与PA 6 gf相比，在预处理状态下，拉伸强度和弹性模量也提高。PA 66 gf50达到铝合金率的16000Mpa-模数。用途：业余爱好工具、电热器盖、电动机、风机冷却螺丝、齿轮、汽车行业的承载部件，如刹车线等。以自然模式和完整RAL色标交付。 Chemically reinforced with 13% glass fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry. With the increasing content of FG also the toughness, tensile and bending strength increase, the shrinkage decreases and the heat application increases up to 250°C. It achieves higher rates of tensile strength and modulus of elasticity also in conditioning state when compared with PA 6 GF. PA 66 GF50 achieves modulus 16000MPa - of the aluminium alloy rates. Application: hobby tools, covers of electrotools, electromotors, cooling screws of blowers, gear wheels, carrying parts in the automotive industry like eg. brake cables. Delivered in natural mode and in the full RAL colour scale. |
产品描述 Product Description
用途：工程配件;电气/电子应用领域;汽车领域的应用;齿轮;
颜色：自然色,可用颜色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 化学耦合; 热稳定性好; 机械强度好; 超高韧性; 耐低温韧性; Good Rigidity,Chemical coupling,Ultra high toughness,Low temperature toughness,Heat Stabilized,HB
填料：玻璃纤维 13
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.19 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
275℃，0.325kg 275℃，0.325kg |
3.0 | g/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
STM 64 0808 | ||
|
TD TD |
0.91 | % | STM 64 0808 |
|
MD MD |
0.88 | % | STM 64 0808 |
|
含水量 water content |
0.15 | % | ISO 960 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
|
-20℃ -20℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
|
-20℃ -20℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/B | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 3146 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
欧洲研讨项目“PUReSmart”的一局部--科思创
2019-01-28 科思创是新的欧洲研究项目“PUReSmart”的一部分，该项目由来自六个国家的九家公司和学术机构组成。其目标是开发一个完整的循环产品生命周期，并将聚氨酯转化为真正可持续的材料。由聚氨酯制成的材料之一是软泡沫和硬泡沫，这是床垫和软垫家具以及建筑绝缘和冷却装置所需的材料。 PUReSmart将运行四年，根据Horizon 2020研究与创新计划(拨款协议编号814543)，将从欧盟获得600万欧元。该项目由比利时Recticel公司协调，旨在回收90%的旧聚氨酯，以便为现有产品 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付