| 牌号简介 About |
|---|
| NANCAR® 1031是一种高丙烯腈-丁二烯共聚物，具有优异的耐油、耐燃料、耐油脂、耐水和耐蒸汽性。它在低温下聚合，并含有足够的抗氧化剂，以满足正常老化条件。NANCAR® 1031推荐用于具有低金属腐蚀性和高耐水性的高耐油橡胶零件。 NANCAR® 1031 is a high acrylonitrile butadiene copolymer with excellent oil, fuel, grease, water and steam resistance. It is polymerized at low temperature and contains sufficient antioxidant for normal aging conditions. NANCAR® 1031 is recommended for use in high oil resistant rubber parts with low metal corrosion and high water resistance. |
产品描述 Product Description
加工条件：注射成型 Injection Molding
性能特点： 耐腐蚀; 耐油; 抗氧化; 共聚物; 吸水率低; 耐蒸汽; 耐燃油; Low or no water absorption,Corrosion Resistant,Inoxidizability,Copolymer,Grease resistance,Resistance to the steam,Fuel resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.998 | g/cm³ | |
|
门尼粘度 Mooney viscosity |
ASTM D1646 | ||
|
ML 1+4，100℃ ML 1+4，100℃ |
63 | MU | ASTM D1646 |
|
ML 1+4，100℃ ML 1+4，100℃ 2 |
79 | MU | ASTM D1646 |
|
丙烯腈含量（Bound） Acrylonitrile content (Bound) |
41.0 | % | 内部方法 |
|
Stabilizer Stabilizer |
Non-staining | ||
|
可溶性 solubility |
|||
|
in MEK in MEK |
% | ||
|
粘度 viscosity |
ASTM D1646 | ||
|
最低限度 Minimum limit |
ASTM D1646 | ||
|
Minutes to 35 points rise，t35 Minutes to 35 points rise，t35 |
min | ASTM D1646 | |
|
Minutes to 5 points rise，t5 Minutes to 5 points rise，t5 |
min | ASTM D1646 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 A，5 秒 Shore A, 5 seconds 3 |
ASTM D2240 | ||
|
邵氏 A，5 秒 Shore A, 5 seconds 4 |
ASTM D2240 | ||
|
邵氏 A，5 秒 Shore A, 5 seconds 5 |
ASTM D2240 | ||
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
300% 应变 300% strain 3 |
MPa | ASTM D412 | |
|
300% 应变 300% strain 4 |
MPa | ASTM D412 | |
|
300% 应变 300% strain 5 |
MPa | ASTM D412 | |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
屈服 yield 3 |
MPa | ASTM D412 | |
|
屈服 yield 4 |
MPa | ASTM D412 | |
|
屈服 yield 5 |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
ASTM D412 | ||
|
断裂 fracture 3 |
% | ASTM D412 | |
|
断裂 fracture 4 |
% | ASTM D412 | |
|
断裂 fracture 5 |
% | ASTM D412 | |
|
撕裂强度 tear strength 6 , 4 |
kN/m | ASTM D624 | |
|
压缩形变 Compression deformation 5 |
|||
|
100℃，70 hr 100℃，70 hr 5 |
% | ASTM D395 | |
|
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
空气中拉伸强度的变化率 The rate of change in tensile strength in air 7 |
|||
|
100℃，70 hr 100℃，70 hr 7 |
% | ASTM D573 | |
|
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air 7 |
|||
|
100℃，70 hr 100℃，70 hr 7 |
% | ASTM D573 | |
|
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air 7 |
|||
|
邵氏 A，100℃，70 hr Shore A, 100 ℃, 70 hr 7 |
ASTM D573 | ||
|
拉伸强度的变化率 The rate of change in tensile strength 7 |
ASTM D471 | ||
|
100℃，70 hr，在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
|
100℃，70 hr，在IRM 903油中 100 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
|
极限伸长率的变化率 Change rate of ultimate elongation 7 |
ASTM D471 | ||
|
100℃，70 hr，在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
|
100℃，70 hr，在IRM 903油中 100 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
|
邵氏硬度的变化率 The rate of change in Shore hardness 7 |
ASTM D471 | ||
|
支撐 A，100℃，70 hr，在ASTM #1油中 Support A, 100 ℃, 70 hr, in ASTM # 1 oil |
ASTM D471 | ||
|
支撐 A，100℃，70 hr，在IRM 903油中 Support A, 100 ℃, 70 hr, in IRM 903 oil |
ASTM D471 | ||
|
体积变化 Volume change 7 |
ASTM D471 | ||
|
100℃，70 hr，ASTM 标准油（1号） 100 ℃, 70 hr, ASTM standard oil (No.1) |
% | ASTM D471 | |
|
100℃，70 hr，在IRM 903油中 100 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热损耗 Heat loss |
% | ASTM D5688 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Uncured |
| 3 CURED @150°C for 60 mins |
| 4 CURED @150°C for 40 mins |
| 5 CURED @150°C for 20 mins |
| 6 C 模具 |
| 7 CURED@150°C × 40 MINUTES |
|
【新闻资讯】查看全部 
科思创计划年内量产零碳足迹聚碳酸酯
2021-04-15 搜料网资讯： 全球化工巨头科思创将试点通过零碳排放的方式，生产其拳头产品。 4月12日，科思创宣布今年三季度将量产全球首款零碳足迹的聚碳酸酯。该产品计划首先在科思创的欧洲 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付