对高茎线有很好的影响,总体平衡很好。 Cardia Biohybrid™ BL-F masterbatch is a homogenous blend of thermoplastic starch (TPS) with polyethylene (PE). This blendable grade is compatibilised to offer a high level of mechanical strength, outstanding elongation properties and toughness. The resin is based on corn starch which is a renewable material. This TPS/PE masterbatch can be blended with a wide range of polyolefin materials to tailor a product with properties perfectly matched to the application. A Biohybrid resin for film applications offering a significant reduction in carbon footprint (compared to PE) An effective contribution to sustainability where biodegradability/compostability is not required. Blendable with LDPE, LLDPE, HDPE and PP resins. Used for thin and thick gauge film and blow moulding applications. Cardia Biohybrid™ BL-F is formulated with 66% of annually renewable starch. This versatile resin is suitable for a wide range of products manufactured by blown film extrusion and extrusion blow molding as well as injection molding processes. Due its content of polyolefins the material is not a compostable polymer and is not intended for ultimate disposal in commercial composting facilities. For applications in which biodegradability/compostability is required we recommend the usage of Cardia Compostable B-F resin. Application Examples Shopping bags/Check-out bags Garbage bags Leaf litter bags Bin liners Overwrap Packaging Disposable or industrial bottles |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.18 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.2 | g/10min | ASTM D1238 |
含水量 water content |
< 0.60 | % | 内部方法 |
生物质含量 Biomass content |
|||
Starch Starch |
66 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D883 | ||
屈服,0.03 mm Yield, 0.03 mm |
> 25.0 | MPa | ASTM D883 |
断裂,0.03 mm Fracture, 0.03 mm |
MPa | ASTM D883 | |
拉伸应变 Tensile strain |
|||
断裂,0.03 mm Fracture, 0.03 mm |
% | ASTM D883 | |
撕裂阻力 Tear resistance |
|||
30.0 µm 30.0 µm |
N | ASTM D1922 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
落锤冲击 Drop hammer impact |
|||
30 µm 30 µm |
g | ASTM D1709 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
蒙迪与汉高合作推出完全可回收的单一材料填充袋
2022-02-11 全球包装和纸张领域的领导者蒙迪(Mondi)和化工企业汉高(Henkel)通过创造全新的重复使用包装概念,帮助消费者更可持续地使用。两家公司合作开发了汉高餐具洗护产品的包装解决 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |