牌号简介 About |
---|
bdt246-2cp是一种中高粘度固化型含氟弹性体三元共聚物。该等级非常适合于要求具有良好加工性能和比标准三元共聚物更好的耐流体性的应用。bdt246-2cp可以复合以满足主要的氟橡胶规格。bdt246-2cp可用于O型圈和垫圈的压缩成型。它可以使用典型的氟弹性体配合剂进行混合。混合可以通过两个辊磨机或内部搅拌机完成。制成品可采用多种橡胶加工方法生产。 BDT246-2CP is a medium to high viscosity curative incorporated fluoroelastomer terpolymer. This grade is well suited for application where good processing properties and superior fluid resistance than standard terpolymers are required. BDT246-2CP can be compounded to meet the major fluoroelastomer specifications. BDT246-2CP can be used for compression molding of O-rings and gaskets. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.86 | g/cm³ | |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
46 | MU | |
氟含量 Fluorine content |
69 | % | |
可溶性 solubility |
LMW Ketones and esters | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness 1 |
|||
邵氏 A Shaw's A 1 |
78 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
屈服 yield 2 |
MPa | ASTM D412 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 3 |
% | ASTM D412 | |
压缩形变 Compression deformation |
|||
200℃,70 hr 200℃,70 hr |
% | ASTM D395B | |
MH(177℃) MH(177℃) 4 |
N·m | ||
ML(177℃) ML(177℃) 5 |
N·m | ||
t'90(177℃) t'90(177℃) 6 |
min | ||
ts2(177℃) ts2(177℃) 7 |
min | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度的变化率 The rate of change in tensile strength |
|||
23℃,168 hr,C级标准燃料 23 ℃, 168 hr, C-grade standard fuel |
% | ASTM D471 | |
极限伸长率的变化率 Change rate of ultimate elongation |
|||
23℃,168 hr,C级标准燃料 23 ℃, 168 hr, C-grade standard fuel |
% | ASTM D471 | |
邵氏硬度的变化率 The rate of change in Shore hardness |
|||
23℃,168 hr,在基准燃料C中 23 ℃, 168 hr, in reference fuel C |
ASTM D471 | ||
体积变化 Volume change |
|||
23℃,168 hr,C级标准燃料 23 ℃, 168 hr, C-grade standard fuel |
% | ASTM D471 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
3 MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
【新闻资讯】查看全部
聚甲醛为什么能用作金属粉末冶金MIM粘结剂?
2015-12-22 MIM全名为金属粉末注射成型,MIM是一种将金属粉末与其粘结剂的增塑混合料注射于模型中的成形方法。今天的故事从PIM开始,PIM全名为粉末注塑成型,它包括金属粉末注射成型(MIM)、陶瓷粉末注射成型(CIM)等。 一、最初的粘结剂都有哪些? 在PIM的发展初期,原料的配方并不是很复杂。任何一个配料工程师都可以去杂货店购买一些石蜡和汽车抛光润滑剂,再添加一些花生油,融化某些塑料(如三明治包装袋),便可以发明一种秘密的粘结剂;然 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |