牌号简介 About |
---|
PMC-746是为制作石膏模而开发的。与PMC-744一样,该产品非常适合用作橡胶箱模具,尤其是需要额外刚性的大型箱模具。肖氏硬度为60 A。由于其耐用性和防潮性能,所以动物园和博物馆也使用PMC-746进行各种模具制作、展示和展览应用。它具有方便的配合比(重量或体积比为2:1),不含汞。其他应用包括制作石膏块模具、复制装饰性石膏(建筑修复)、预制混凝土模具、铸造蜡、光滑硬质聚氨酯和环氧树脂,以及制作电影和剧院的各种特殊效果。 PMC®-746 was developed to make molds for casting gypsum plasters. Like PMC®-744, this product is well suited for use as a rubber case mold - especially large case molds where extra rigidity is required. Shore hardness is 60 A. Because of its durability and moisture resistant properties PMC®-746 is also used by zoos and museums for a variety of mold-making, display and exhibit applications. It features a convenient mix ratio (2:1 by weight or volume), and contains no mercury. Other applications include making plaster block molds, reproducing ornamental plaster (architectural restoration), pre-cast concrete molds, casting waxes, Smooth-On rigid polyurethanes and epoxies and also for making a variety of special effects for movies and theatre. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.03 | g/cm³ | ASTM D1475 |
特定体积 Specific volume |
0.972 | cm³/g | |
收缩率 Shrinkage rate |
|||
MD MD |
< 0.10 | % | ASTM D2566 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
60 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
4.83 | MPa | ASTM D412 |
100% 应变 100% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
储存稳定性 storage stability |
|||
23℃ 23℃ |
min | ASTM D2471 | |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脱模时间 stripping time |
|||
23℃ 23℃ |
min | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
混合比 Mixing ratio |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部
新树脂资料 推进行业使用
2016-02-25 研发实力是一个企业的持久竞争力,对于塑化行业的巨头们如是。通过研发推出新树脂材料,既提升公司研发竞争力,又为行业提供性能更优越的材料,推进行业应用。 杜邦制成聚酯有望替代PET 杜邦公司的工业生物科学业务部和ArcherDanielsMidlandCo.(ADM)公司合作开发出一种技术,有望带来一种崭新的可持续发展树脂,成为PET的替代材料。合作双方表示,他们发现了一种突破性的工艺,由此生产出的单体能取代对苯二甲酸,这是聚对 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |