杜邦Nucrel® 3990是乙烯和丙烯酸的共聚物,通常由9.5 wt%丙烯酸制成。它可用于传统的挤出涂料,共挤涂料和挤出层压设备设计加工聚乙烯树脂。 DuPont™ Nucrel® 3990 is a copolymer of ethylene and acrylic acid made with nominally 9.5 wt% acrylic acid. It is available for use in conventional extrusion coating, coextrusion coating and extrusion laminating equipment designed to process polyethylene resins. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ASTM D792 |
密度 Density |
0.940 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
10 | g/10min | ASTM D1238 |
190℃,2.16kg 190℃,2.16kg |
10 | g/10min | ISO 1133 |
丙烯酸含量 Acrylic acid content |
9.5 | wt% | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
冰点 freezing point 2 |
|||
-- -- |
℃ | ISO 3146 | |
-- -- |
℃ | ASTM D3418 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 DSC |
【新闻资讯】查看全部
供需格局偏紧,动力煤市场偏强运行
2021-05-02 搜料网资讯: 【导语】年后动力煤市场先抑后扬,尤其是进入3月份后,受供需格局偏紧因素影响,动力煤市场快速止跌企稳并反弹,短时间市场热情高涨,煤价涨幅较大。 年后动力煤 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |