牌号简介 About |
---|
Ryton® R-4-220NA和R-4-220BL 40%玻璃纤维增强聚苯硫醚化合物在持续或反复暴露于高温水中后提供增强的机械强度。 Ryton® R-4-220NA and R-4-220BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength after constant or repeated exposure to high temperature water. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.68 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
TD:3.2 mm TD:3.2 mm |
0.50 | % | |
MD:3.2 mm MD:3.2 mm |
0.20 | % | |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.020 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
9.0 | kJ/m² | ISO 180/A |
3.2mm 3.2mm |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
kJ/m² | ISO 180 | |
3.2 mm 3.2 mm |
J/m | ASTM D4812 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
ASTM E831 | ||
-50 到 50℃ -50 to 50 ℃ |
cm/cm/℃ | ASTM E831 | |
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
MD MD |
ASTM E831 | ||
-50 到 50℃ -50 to 50 ℃ |
cm/cm/℃ | ASTM E831 | |
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ||
UL温度额定值 UL temperature rating |
℃ | UL 746B | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
25 ℃,1 kHz 25 ℃,1 kHz |
ASTM D150 | ||
25 ℃,1 MHz 25 ℃,1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
25℃,1 kHz 25℃,1 kHz |
ASTM D150 | ||
25℃,1 MHz 25℃,1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
水解稳定性 Hydrolysis stability 2 |
|||
拉伸强度 Retained Tensile strength Retained |
% | ||
体重增量 Weight gain |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
泊松比 Poisson's ratio |
ISO 527 | ||
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Test specimens aged 1000 hours in water at 140°C (284°F) |
【新闻资讯】查看全部
《腐植酸基础产品生产行业保价稳市自律公约》发布
2022-03-06 2月25日,中国腐植酸工业协会发布了《腐植酸基础产品生产行业保价稳市自律公约》,倡议遵照执行十个必须,构建良好的腐植酸基础产品市场环境,坚决打击假冒伪劣产品、无序化竞 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |