牌号简介 About |
---|
Somos® PerFORM在标准355nm立体光刻机上生产强度高、硬度高、耐高温的复合材料部件。这种材料的低粘度使加工零件更快。与其他复合立体光刻材料相比,该材料具有优异的侧壁质量和良好的细节分辨率。应用Somos® PerFORM是一种易于加工的材料,具有出色的细节分辨率。它是制造具有优异耐热性的坚固、坚硬部件的理想材料,包括航空航天和汽车应用的风洞模型,以及用于注塑的快速模具。 Somos® PerFORM produces strong, stiff, high-temperature resistant composite parts on standard 355 nm stereolithography machines. This material's lower viscosity makes processing parts faster. It exhibits superior sidewall quality, along with excellent detail resolution compared to other composite stereolithography materials. Applications Somos® PerFORM is an easy to process material with excellent detail resolution. It is the ideal material for creating strong, stiff parts with excellent high heat resistance, including wind tunnel models for aerospace and automotive applications, as well as rapid tooling for injection molding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.61 | g/cm³ | |
吸水率 Water absorption rate |
ASTM D570 | ||
平衡 balance 2 |
0.20 | % | ASTM D570 |
平衡 balance 3 |
0.10 | % | ASTM D570 |
粘度 viscosity |
|||
30℃ 30℃ |
1.00 | Pa·s | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-- -- 2 |
17 | J/m | ASTM D256 |
-- -- 3 |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
1.8 MPa,未退火 1.8 MPa, unannealed 3 |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed 2 |
℃ | ASTM D648 | |
玻璃化转变温度 Glass transition temperature |
ASTM E1545 | ||
-- -- 2 |
℃ | ASTM E1545 | |
-- -- 3 |
℃ | ASTM E1545 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
ASTM E831 | ||
-40 到 0℃ -40 to 0 ℃ 3 |
cm/cm/℃ | ASTM E831 | |
-40 到 0℃ -40 to 0 ℃ 2 |
cm/cm/℃ | ASTM E831 | |
0 到 50℃ 0 to 50 ℃ 3 |
cm/cm/℃ | ASTM E831 | |
0 到 50℃ 0 to 50 ℃ 2 |
cm/cm/℃ | ASTM E831 | |
50 到 100℃ 50 to 100 ℃ 3 |
cm/cm/℃ | ASTM E831 | |
50 到 100℃ 50 to 100 ℃ 2 |
cm/cm/℃ | ASTM E831 | |
100 到 150℃ 100 to 150 ℃ 2 |
cm/cm/℃ | ASTM E831 | |
100 到 150℃ 100 to 150 ℃ 3 |
cm/cm/℃ | ASTM E831 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
ASTM D149 | ||
-- -- 2 |
kV/mm | ASTM D149 | |
-- -- 3 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz 2 |
ASTM D150 | ||
1 kHz 1 kHz 3 |
ASTM D150 | ||
1 kHz 1 kHz 2 |
ASTM D150 | ||
1 MHz 1 MHz 2 |
ASTM D150 | ||
1 MHz 1 MHz 3 |
ASTM D150 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Critical Exposure Critical Exposure |
mJ/cm² | ||
渗透深度 Penetration depth |
µm | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 D Shaw's D 2 |
ASTM D2240 | ||
邵氏 D Shaw's D 3 |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
ASTM D638 | ||
-- -- 2 |
MPa | ASTM D638 | |
-- -- 3 |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
ASTM D638 | ||
-- -- 2 |
MPa | ASTM D638 | |
-- -- 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
断裂 fracture 2 |
% | ASTM D638 | |
断裂 fracture 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
-- -- 2 |
MPa | ASTM D790 | |
-- -- 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
-- -- 2 |
MPa | ASTM D790 | |
-- -- 3 |
MPa | ASTM D790 | |
泊松比 Poisson's ratio |
ASTM D638 | ||
-- -- 2 |
ASTM D638 | ||
-- -- 3 |
ASTM D638 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 UV Postcure & Thermal Postcure |
3 UV Postcure |
【新闻资讯】查看全部
再生塑料:处于风口中 你将如何应对一刀切?
2017-04-28 近期习近平主持召开中央全面深化改革领导小组第三十四次会议,会议审议通过了《关于禁止洋垃圾入境推进固体废物进口管理制度改革实施方案》。“禁止固体废物进口”又一次被推到了风口浪尖上。 集中市场处于整顿进行时 < |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |