SABIC® LLDPE 726Q是一种丁烯线性低密度聚乙烯树脂。这一等级通常被设计为使吹塑薄膜具有相对较高的刚度,从而具有良好的可加工性和其他性能(如耐穿刺性、冲击强度和热密封性)的良好总体平衡性。这种材料含有防堵、防滑剂和加工助剂。SABIC® LLDPE 726Q的典型应用是运输袋、生产袋、罐衬和运输袋。SABIC® LLDPE 726Q与低密度聚乙烯(15-85%)混合时具有良好的光学性能。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® LLDPE 726Q is a butene linear low density polyethylene resin. This grade is typically designed to give blown films a relatively high stiffness for good machinability and a good overall balance of other performance properties, such as puncture resistance, impact strength and heat sealability. This material contains anti block, slip erucamide and processing aid. Application Typical applications for SABIC® LLDPE 726Q are shipping sacks, produce bags, can liners and carrier bags. SABIC® LLDPE 726Q has good optical properties when blended with a LDPE (15-85%). This product is not intended for and must not be used in any pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.926 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.70 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
0.10 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
拉伸模量 Tensile modulus |
ISO 527-3 | ||
MD,50 µm,吹塑薄膜 MD, 50 µ m, blow molded film |
220 | MPa | ISO 527-3 |
TD,50 µm,吹塑薄膜 TD, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁冲击强度 Izod notched impact strength |
|||
50µm,吹塑成型 50 µ m, blow molded |
J/cm | ASTM D4272 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.0 µm,吹塑薄膜 45 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻塞力 Blocking force |
|||
吹塑薄膜,50.0 µm Blow molded film, 50.0 µ m |
g | 内部方法 | |
抗穿刺性 Puncture resistance |
|||
吹塑薄膜,50.0 µm Blow molded film, 50.0 µ m |
J/m | 内部方法 | |
Re-blocking - 吹塑薄膜(50.0 µm) Re blocking - blow molded film (50.0 µ m) |
g | 内部方法 | |
撕裂强度 tear strength 2 |
ISO 6383-2 | ||
MD,50 µm MD,50 µm |
kN/m | ISO 6383-2 | |
TD,50 µm TD,50 µm |
kN/m | ISO 6383-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Blown Film |
【新闻资讯】查看全部
无净化废旧塑料柔性油化工艺设备降生
2017-07-18 根据7月16日消息,三河市福海特种设备制造有限公司研发出一套可实现无污染废旧塑料柔性油化的工艺设备。它的研发成功,破解了塑料垃圾处理的难题,实现了处理过程无污染,同时垃圾变能源,催生废旧塑料的更大价值,而且经过简单加工,98%的原料油都将成为供生产生活使用的柴油或汽油,油品质量达到国家标准。 在今年5月28日国务院发展研究中心“废塑料能源化利用研究”研讨会上,这套工艺得到了环保部固体废物管理中心、国家发改委、清华大学的专家认可。其中,中国工程院院士、清华大学化学科学与技术研 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |