Safron® H504-12M聚丙烯树脂被推荐用于2-25丹尼尔范围内的短纤维纺纱。它也用于制造BCF纱。Safron® H504-12M聚丙烯树脂是一种中高流动注射成型等级,适用于刚性和快速循环时间至关重要的应用。 Safron® H504-12M Polypropylene Resin is recommended for the spinning of staple fibre in the range 2 — 25 denier. It is also used for the manufacture of BCF yarns. Safron® H504-12M Polypropylene Resin is a medium to high flow injection moulding grade for applications where rigidity and fast cycle times are essential. Typical Process Applications High tenacity yarns Staple fibres End Use Applications Needle punched floor coverings Tufted carpets |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
12 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,注塑成型 Yield, injection molding |
30.0 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
屈服,注塑成型 Yield, injection molding |
7.5 | % | ISO 527-2 |
弯曲模量 Bending modulus |
|||
注塑成型 injection molding |
1360 | MPa | ISO 178 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Injection Molded |
【新闻资讯】查看全部
抗洪精神:将团结奋斗的基因融入血脉
2021-11-20 搜料网资讯: 1998年夏,一场始料未及的特大洪水席卷我国江南、华南大部分地区及北方局部地区。正是在那时,中国人民开展了气势恢宏、艰苦卓绝的抗洪抢险斗争,形成了万众一心、 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |