牌号简介 About |
---|
LLC6-200是一种经认证的主要树脂,设计用于注塑成型,要求在各种成型条件下具有低翘曲、耐低温和易加工性。建议加工温度为180至220°C,模具温度为20至40°C。 LLC6-200 is a certified prime resin designed for injection molding applications requiring low warpage, low temperature resistance and easy processability over a wide range of molding conditions. Recommended processing temperature is 180 to 220°C., with mold at 20 to 40°C. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.924 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
20 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
50 ℃,F50 50 ℃,F50 |
19.0 | hr | ASTM D1693 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
屈服 yield 2 |
12.4 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
500 | % | ASTM D638 |
弯曲模量 Bending modulus 3 |
|||
1% 正割 1% secant 3 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸冲击强度 Tensile impact strength |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.051 in/min |
【新闻资讯】查看全部
十部门:全面系统加强塑料污染全链条治理
2020-10-12 搜料网资讯:9月11日,国家发展改革委、生态环境部等十部门举行了全国塑料污染治理工作会,对当前我国塑料污染治理进展以及下一步在哪些方面发力作出了部署。 会议指出,塑料污 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |