| 牌号简介 About |
|---|
| Baytec MS-052是一种改性二苯基甲烷二异氰酸酯（MDI）端接聚酯预聚物，用于制造高性能固体浇注聚氨酯弹性体。当与1,4-丁二醇混合时，该材料符合FDA法规21 CFR 177.2600（重复使用的橡胶制品），可用于干湿重复使用的食品接触应用。当与hqee一起使用时，它符合21 CFR 177.1680（聚氨酯树脂），并且只能用于重复使用的食品接触没有自由表面脂肪或油的干燥食品。与任何产品一样，在给定应用中使用Baytec MS-052预聚物必须由用户提前测试（包括现场测试等），以确定其适用性。 Baytec MS-052 is a modified diphenylmethane diisocyanate (MDI)-terminated polyester prepolymer used in the manufacture of high-property solid cast polyurethane elastomers. When extended with 1,4-butanediol, this material complies with FDA regulation 21 CFR 177.2600 (Rubber Articles Intended for Repeated Use) and may be used for wet and dry repeated-use food-contact applications. When extended with HQEE, it complies with 21 CFR 177.1680 (Polyurethane Resins) and may be used for repeated-use food contact only with dry foods having no free surface fats or oils. As with any product, use of Baytec MS-052 prepolymer in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
产品描述 Product Description
| 技术参数 Technical Data | |||
|---|---|---|---|
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
断裂 fracture |
26.3 | MPa | ASTM D412 |
|
100% 应变 100% strain |
8.34 | MPa | ASTM D412 |
|
200% 应变 200% strain |
10.6 | MPa | ASTM D412 |
|
300% 应变 300% strain |
12.5 | MPa | ASTM D412 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
650 | % | ASTM D412 |
|
撕裂强度 tear strength |
|||
|
-- -- 2 |
kN/m | ASTM D624 | |
|
开裂 cracking |
kN/m | ASTM D1938 | |
|
压缩形变 Compression deformation |
|||
|
70℃，22 hr 70℃，22 hr |
% | ASTM D395 | |
|
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A Shaw's A |
ASTM D2240 | ||
|
泰伯耐磨性 Taber abraser |
|||
|
1000 周期，1000 g，H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ASTM D4066 | |
|
压缩变形 compression deformation |
ASTM D575 | ||
|
10% 10% |
MPa | ASTM D575 | |
|
15% 15% |
MPa | ASTM D575 | |
|
2% 2% |
MPa | ASTM D575 | |
|
20% 20% |
MPa | ASTM D575 | |
|
25% 25% |
MPa | ASTM D575 | |
|
5% 5% |
MPa | ASTM D575 | |
|
50% 50% |
MPa | ASTM D575 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 C 模具 |
|
【新闻资讯】查看全部
联合国拟成立专家组讨论陆地塑料渣滓对策
2018-01-23 据相关人士20日透露，作为应对海洋塑料垃圾及“微塑料”这一国际性大问题的对策，联合国将首次成立专家组，讨论具体的削减方法和替代品，以及采取对策所面临的课题等。据分析全球每年有约1000万吨塑料垃圾流入海洋，此举旨在推动各国从根本上强化对策。 专家组为实现削减垃圾，将讨论包括具有法律约束力的国际条约在内的政策面选项。还将分析塑料替代品的性能、费用及普及的问题点等，汇总有关对策的建议。力争向近年问题尤其严重的发展中国家提出有效的对策。 联合国将基于各国政府等的推 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付