牌号简介 About |
---|
说明:SPB681是一种采用高压技术生产的低密度聚乙烯。用该产品获得的薄膜显示出优异的“拉伸”、良好的密封性和低的凝胶含量。不含添加剂。该等级的最低生物基含量为95%,根据ASTM D6866测定。用途:LLDPE和HDPE共混物。工艺:吹塑和铸膜挤出。注射成型。 Braskem PE SPB681 SPB681 is a low density polyethylene produced under high pressure technology. Films obtained with this product show excellent 'draw down', good sealability, and low gel content. Additives free. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Applications: LLDPE and HDPE blends. Flexible containers for cosmetics and pharmaceutical applications (complies with USP 37). Process: Blown and Cast Film Extrusion. Injection molding. Braskem PE SPB681 SPB681 is a low density polyethylene produced under high pressure technology. Films obtained with this product show excellent 'draw down', good sealability, and low gel content. Additives free. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Applications: LLDPE and HDPE blends. Flexible containers for cosmetics and pharmaceutical applications (complies with USP 37). Process: Blown and Cast Film Extrusion. Injection molding. Braskem PE SPB681 SPB681 is a low density polyethylene produced under high pressure technology. Films obtained with this product show excellent 'draw down', good sealability, and low gel content. Additives free. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Applications: LLDPE and HDPE blends. Flexible containers for cosmetics and pharmaceutical applications (complies with USP 37). Process: Blown and Cast Film Extrusion. Injection molding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.922 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.8 | g/10min | ASTM D1238 |
Biobased Content Biobased Content |
95 | % | ASTM D6866 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
20.0 | MPa | ASTM D882 |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
30.0 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
TD,38 µm,吹塑薄膜 TD, 38 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,38.0 µm,吹塑薄膜 60 °, 38.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
医疗革命:欧盟开发细菌“超级杀手”布
2016-01-18 医院病房和公共场所是细菌交叉感染的“重灾区”,尤其是近年来欧盟医院屡屡频发的细菌病原体交叉感染事件,引起欧委会和医学科技界的高度关注。 近日,欧盟第七研发框架计划(FP7)资助110万欧元,由10家创新型中小企业(SMEs)联合医学科技界组成的欧洲CLEANWARD研发团队,成功研制开发出一款全新的医院病房细菌“超级杀手”,可100%杀死任何细菌或微生物病原体。 该团队创新的开发出全新微细纤维纺织物(Microfibre Fabric)和二氧化钛(TiO2) |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |