牌号简介 About |
---|
洛夫克斯A3110聚酯薄膜具有光学透明性,单侧电晕处理,拉伸强度高,延伸率好,热收缩率高等优点。由于其运行良好,易于用合适的产品处理,可作为广告材料使用。另外,它是一种可以根据客户需求进行厚度控制的产品。 LOFEX ® A3110 Polyester film is optically clear and one side corona treated with excellent properties by tensile strength , proper elongation and the thermal contraction rate. It can use by advertisement material because it has excellent run, easy treatment by suitable product. Also, it is a product that thickness control is possible according to customer needs. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面张力 surface tension |
|||
100.0 µm 100.0 µm |
52 | mN/m | |
175.0 µm 175.0 µm |
52 | mN/m | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态 With oneself - dynamic |
0.29 | ASTM D1894 | |
与自身 - 静态 With oneself - static |
0.32 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,100 µm MD, yield, 100 µ m |
196 | MPa | ASTM D882 |
MD,屈服,180 µm MD, yield, 180 µ m |
MPa | ASTM D882 | |
TD,屈服,100 µm TD, yield, 100 µ m |
MPa | ASTM D882 | |
TD,屈服,180 µm TD, yield, 180 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,100 µm MD, fracture, 100 µ m |
% | ASTM D882 | |
MD,断裂,180 µm MD, fracture, 180 µ m |
% | ASTM D882 | |
TD,断裂,100 µm TD, fracture, 100 µ m |
% | ASTM D882 | |
TD,断裂,180 µm TD, fracture, 180 µ m |
% | ASTM D882 | |
F5 F5 |
ASTM D882 | ||
MD:100.0 µm MD:100.0 µm |
MPa | ASTM D882 | |
MD:175.0 µm MD:175.0 µm |
MPa | ASTM D882 | |
TD:100.0 µm TD:100.0 µm |
MPa | ASTM D882 | |
TD:175.0 µm TD:175.0 µm |
MPa | ASTM D882 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D523 | ||
60°,100 µm 60°,100 µm |
ASTM D523 | ||
60°,175 µm 60°,175 µm |
ASTM D523 | ||
透光率 Transmittance |
ASTM D1003 | ||
100 µm 100 µm |
% | ASTM D1003 | |
175 µm 175 µm |
% | ASTM D1003 | |
雾度 Haze |
ASTM D1003 | ||
100 µm 100 µm |
% | ASTM D1003 | |
175 µm 175 µm |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热收缩 Thermal shrinkage |
内部方法 | ||
MD,30 min:150℃,100.0 µm MD,30 min:150℃,100.0 µm |
% | 内部方法 | |
MD,30 min:150℃,175.0 µm MD,30 min:150℃,175.0 µm |
% | 内部方法 | |
TD,30 min:150℃,100.0 µm TD,30 min:150℃,100.0 µm |
% | 内部方法 | |
TD,30 min:150℃,175.0 µm TD,30 min:150℃,175.0 µm |
% | 内部方法 | |
Surface Treatment Surface Treatment |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
研究发现环保餐具对海洋动物依然有害
2020-11-06 搜料网资讯: 特拉维夫大学的一项新研究比较了两种一次性餐具对海洋环境的影响普通塑料一次性餐具和经各种国际组织认证的更昂贵的生物塑料一次性餐具,并确定生物塑料餐具对海 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |