牌号简介 About |
---|
ADIPRENE L 767是一种以TDI聚醚为基础的液体聚氨酯预聚物,通过传统的手工和机械混合技术可以很容易地加工。当用4,4’-亚甲基双(2-氯苯胺)固化时,adiprene L767可生产62d硬度范围内的高质量弹性体;当用Caytur 21da固化时,adiprene L767可生产53d硬度范围内的高质量弹性体。这些坚韧、高弹性的弹性体有许多独特的特点:优异的低温弹性?-优异的耐磨性?-良好的水解稳定性?-良好的抗压缩永久变形性能。这些性能表明,在车轮、辊或喷涂等应用中使用了Adiprene L 767。 ADIPRENE L 767 is a TDI polyether-based liquid urethane prepolymer which is readily processable by conventional hand and machine mixing techniques. ADIPRENE L767 produces high quality elastomers in the 62D durometer hardness range when cured with 4,4'-methylene-bis (2-chloroaniline), and the 53 D durometer hardness range when cured with CAYTUR® 21DA. These tough, highly resilient elastomers have many unique features: Excellent low-temperature flexibility ?- Excellent abrasion resistance ?- Good hydrolytic stability ?- Good compression set resistance These properties suggest the use of ADIPRENE L 767 in applications such as wheels, rolls, or spraying. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.14 | g/cm³ | ASTM D792 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
62 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
44.8 | MPa | ASTM D412 |
100% 应变 100% strain |
18.6 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
290 | % | ASTM D412 |
撕裂强度 tear strength |
|||
开裂 cracking |
kN/m | ASTM D470 | |
压缩形变 Compression deformation |
|||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
卡-伯模量 Kappa's modulus |
ASTM D1043 | ||
-57℃ -57℃ |
MPa | ASTM D1043 | |
-40℃ -40℃ |
MPa | ASTM D1043 | |
-18℃ -18℃ |
MPa | ASTM D1043 | |
24℃ 24℃ |
MPa | ASTM D1043 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
储存稳定性 storage stability |
min | ||
后固化时间 Post curing time |
|||
70℃ 70℃ |
hr | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
NBS NBS |
|||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
100℃ 100℃ |
hr |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
东丽兼并位于塔科马和美国阿拉斯加州的公司业务
2017-04-11 碳纤维和预浸料制造商 Toray Industries Inc.(日本东丽)于4月3日对外宣布,正在巩固其北美碳纤维复合材料业务。具体措施为,将位于塔科马的东丽复合材料公司(TCA)和位于美国阿拉斯加州迪凯特的东丽碳纤维美 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |