| 牌号简介 About |
|---|
| Casico™ FR4804是一种热塑性、低烟无卤（LSZH）阻燃、紫外线稳定的天然护套化合物，具有优异的挤出性能。它是基于一种新型的技术，即含有无机填料的CASICO和一种新型的成炭添加剂，这种添加剂具有阻燃性，且烟雾生成非常有限。它可用于对烟雾或腐蚀性和有毒燃烧产物敏感的区域。Casico™ FR4804符合以下使用良好的商业挤压实践和测试程序的适用要求：BS 7655 LTS2 EN 50173 EN 50290-2-27 EN 50363-8 TM7 IEC 60227 VDE 0207 TEIL 24（hm2、hm4和hm5）VDE 0250 TEIL 215 Casico FR4804 is a thermoplastic, low smoke zero halogen (LSZH) flame retardant, UV stabilised, natural jacketing compound combining with excellent extrusion properties. It is based on the novel technology, Casico, containing inorganic filler and a novel char-forming additive which confer flame retardancy with very limited smoke generation. Applications Casico FR4804 is designed for: Jacket for data cables and 90 °C rated jacket for energy distribution cables. It can be used in areas sensitive to smoke or corrosive and toxic combustion products. Specifications Casico FR4804 meets the applicable requirements below using sound commercial extrusion practice and testing procedures: ASTM D 1248 Type I, Class A, Category 4 ISO 1872-PE KGHN-23D006 The following cable material standards are met by Casico FR4804: EN 50290-2-27 EN 50363-8 TM7 VDE 0207 Teil 24 (HM2, HM4 & HM5) BS 7655 LTS2 Cables manufactured with Casico FR4804 using sound extrusion practice normally comply with the following cable product standards: EN 50288 VDE 0250 Teil 215 BS 7211 IEC 60502 Part 1 ST3 Special features Casico FR4804 consists of specially selected components to offer: Low smoke and reduced toxic or corrosive gas emissions Excellent processing properties Superb system ageing compatibility Low water permeability UV stabilised and suitable for colouring Possibility for cable downsizing Processability on most PVC/PE extrusion equipment No need for pre-drying normally |
产品描述 Product Description
用途：电缆护套;电线电缆应用;
颜色：自然色
加工条件：挤出 Extrusion
性能特点： 无卤; 耐腐蚀; 低烟; 防潮; 着色性好; 阻燃; 耐候抗UV; 毒性低; 易加工; Weather resistance is good,Excellent Processability,Low smoke,Halogen free,Corrosion Resistant,Flame Characteristics,Low toxicity,Moisture resistance,Good coloring
紫外线：UV Stabilized
填料：其他
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density 3 |
1.15 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate 3 |
|||
|
190℃，2.16kg 190℃，2.16kg 3 |
0.40 | g/10min | ISO 1133 |
|
吸水率 Water absorption rate 4 |
|||
|
70℃ 70℃ 4 |
0.100 | mg/cm² | IEC 60811-1-3 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness 3 |
|||
|
邵氏 D，15 秒 Shore D, 15 seconds 3 |
39 | ISO 868 | |
|
拉伸强度 tensile strength 5 , 6 |
|||
|
屈服 yield 5 , 6 |
11.0 | MPa | IEC 60811-1-1 |
|
拉伸应变 Tensile strain 6 |
|||
|
断裂 fracture 6 |
% | IEC 60811-1-1 | |
|
弯曲模量 Bending modulus 3 |
MPa | ISO 178 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
低温弯曲 Low temperature bending 6 |
|||
|
-40℃ -40℃ 6 |
IEC 60811-1-4 | ||
|
低温冲击 Low temperature shock 6 |
|||
|
-40℃ -40℃ 6 |
IEC 60811-1-4 | ||
|
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度的变化率 The rate of change in tensile strength |
IEC 60811-1-2 | ||
|
-- -- 7 |
% | IEC 60811-1-2 | |
|
100℃，240 hr 100℃，240 hr 6 |
% | IEC 60811-1-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity 3 |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
极限氧指数 Extreme oxygen index |
% | ||
|
NBS烟雾密度 NBS smoke density |
ASTM E662 | ||
|
-- -- 8 |
ASTM E662 | ||
|
-- -- 9 |
ASTM E662 | ||
|
time to Dmax time to Dmax 9 |
min | ASTM E662 | |
|
time to Dmax time to Dmax 10 |
min | ASTM E662 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Breakdown Duration Breakdown Duration 6 |
IEC 60227-2/2.3 | ||
|
击穿电压 breakdown voltage 6 |
V | ISO 6722 | |
|
锥形量热试验 Cone calorimetry test |
ISO 5660 | ||
|
平均热释放速率 Average heat release rate 11 |
kW/m² | ISO 5660 | |
|
CO CO 11 |
g/cm³ | ISO 5660 | |
|
CO2 CO2 11 |
g/cm³ | ISO 5660 | |
|
燃烧热 Combustion heat 12 |
ISO 5660 | ||
|
Ingition time Ingition time 11 |
min | ISO 5660 | |
|
最大热释放速率 Maximum heat release rate 11 |
kW/m² | ISO 5660 | |
|
Smoke Obscuration Smoke Obscuration 13 |
ISO 5660 | ||
|
Corrosion（of Combustion Fumes） Corrosion（of Combustion Fumes） 14 |
µS/cm | ||
|
热压测试 Hot pressing test 15 |
|||
|
90℃ 90℃ 15 |
% | IEC 60811-3-1 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Compound, ISO 1872-2 |
| 3 Compound |
| 4 Cable (0.7 mm insulation over 1.5 mm² solid Cu), 14 days |
| 5 2.0 in/min |
| 6 Cable (0.7 mm insulation over 1.5 mm² solid Cu) |
| 7 After UV ageing |
| 8 Flaming mode, Optical Smoke Density Dmax, (76x76x0.7 mm plaque) |
| 9 Non- flaming mode, Optical Smoke Density Dmax, (76x76x0.7 mm plaque) |
| 10 Non-flaming mode, Optical Smoke Density Dmax, (76x76x0.7 mm plaque) |
| 11 heat flux 35 kW/m2, 3 mm plaque |
| 12 heat flux 35 kW/m2, 3 mm plaque, MJ/dm3 |
| 13 heat flux 35 kW/m2, 3 mm plaque, m2/dm3 |
| 14 Compound, 5.3 |
| 15 at high temperature, 4 hrs, Cable (0.7 mm insulation over 1.5 mm² solid Cu) |
|
【新闻资讯】查看全部
索尔维推进先进聚合物在3D打印中的成功使用
2018-08-13 随着KetaSpire PEEK AM高性能长丝将成为第一个被纳入到Digimat仿真软件中的聚醚醚酮聚合物，索尔维进一步确立了其作为一家为增材制造(AM)提供特种聚合物的新兴领导者的地位。 e-Xstream engineering公司将于2018年6月发布Digimat仿真软件。 “KetaSpire PEEK被纳入到Digimat软件中，代表了索尔维在为推动先进聚合物在3D打印中的成功应用、从而令自身发展成为行业领先者方面而迈出了新的一步。”索尔维特种 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付